1.       STANDARD

 

the concentric conductors of copper and aluminum, is entirely consistent with the rules ASTM D 790, D 1248, D 2655, D 2656, UL 854, UL 44, .

 2.        CHARACTERISTICS OF THE COPPER  CONDUCTORS

 

2.1 CONSTRUCTIVE CHARACTERISTICS

 

Each material used in the conductor will be compatible with all other materials used in the manufacture of concentric conductor.

 

Concentric conductor consists of one or two conductors which in turn are coated with a bare conductor distributed helically around the conductors.

 

According to these configurations will have a phase and outer concentric neutral (bipolar), or two phases and these external neutral (tripolar)

 

Section of all conductors that form the concentric conductor of both phases as the concentric neutral is the same.

 

Conductor:

 

The materials used in the manufacture of concentric copper conductors formed by wires keychain copper

 

copper  shall comply with the provisions of ASTM B 3 standard and UL 854.

 

 

In the phase conductors with 7 wires, will be able to perform welding wires during wiring. Once this process is completed it will not be allowed two welds closer than 15m (50ft)

 

According to paragraph 6 of ASTM B 8, the wiring process will be as follows:

Over the central conductor will be braided the rest of the layers. Braiding step will be at a distance to vary between 8 and 16 times the outside diameter. The lay direction of the  wires in the outer layer will be right.

 

Isolation:

 Each phase conductor will contain an insulating layer of PE for a temperature of 90 C. in the bipolar cables, over the insulating layer will be the braided neutral conductor helically with a passage between 8 and 16 times the outer diameter. In the tripolar cables over the isolation of each phase will have a PVC insulation filling in the joint of both cables and over this will be placed the neutral conductor.

 

 Will be put over the concentric neutral conductor a tape and over this outer layer of PE. Must ensure the tightness of the set plus adequate resistance to ultraviolet rays (UV).

 

This last layer besides adding firmness should be smooth in appearance and will not be observed depressions caused by unfilled spaces beneath this layer.

 

Should not produce bubbles, cuts, tears or the presence of foreign materials that are detectable to the naked eye. Besides the envelope will be well centered.

 

The disposition of the tape around the bare conductor shall be performed as follows:

 

A single layer of tape with a convenient width helically applied without wrinkles or folds and with an overlap of at least 6mm.  The tape will consist of nylon, with a thickness of at least 0.09mm.

 

Covering the entire concentric conductor will be placed a PE coating.

 

CONCENTRIC CONDUCTORS  AL
FEATURES		#8 x 2	#8 x 3	#6 x 3	#4 x 3	#2 x 3
Phase	Material	Al	Al	Al	Al	Al
	No. Of wires	7	7	7	7	7
	Wire diameter  (m.m.)	1,234	1,234	1,555	1,961	2,473
	phase diameter (m.m.)	3.71	3.71	4.67	5.89	7.42
	Phase area  (mm²)	8,367	8,367	13.3	21.15	33.62
	Nominal electrical resistance  C.C. a 20°C Ohm/Km.	3.43	3.43	2.16	1.36	0.855
	Nominal weight Kg/Km	22.69	22.69	247	57.37	91.21
	Ampacity  (A)	45	45	60	75	100
	Phase Insulation thickness (m.m.) (PE)	1.14	1.14	1.14	1.14	1.14
	Diameter over insulation	5.99	5.99	6.95	8.17	9.7
Neutral	No. Of wires	37	37	37	65	65
	Wire diameter  (m.m.)	0.536	0.536	0.676	0.643	0.823
	Area of Neutral (mm²)	8.349	8.349	13.280	21.107	34.578
Interior Nylon tape thickness (mm²)		0.05
Exterior Thickness for PE cover (mm²)		1.14	1.14	1.14	1.14	1.14