1. Specification

INCI NAME: Carbomer

APPEARANCE: White fluffy powder

Oder: Slightly acetic

CAS No.: 9003-01-4

 

Parameter	Solution	Value	Test Frequency
Viscosity/ mPa.s(20 rpm at 25ºC, Neutralized Solution)	0.5% Water solution	65,000-75,000	Each Lot
Solution Clarity /% (Neutralized Solution 420 nm wavelength)	0.5% Water solution	≥85	Each Lot
Residual Benzene /%	--	≤0.50	Each Lot
Residual acrylic acid/%	--	≤0.25	Once/10 Lots
Loss on drying/%	--	≤2.0	Once/10 Lots
Bulk Density/(g/100 mL)	--	21.0-27.0	Once/10 Lots
Heavy metal Pb+As+Hg+Sb (ppm)	--	≤10	Once/200Lots

 

   

2. Technical Data   

NM-Carbomer 996 is a cross-linked polyacrylate polymer. It is used as a high-efficient rheology modifier, capable of providing high viscosity, excellent thickening and suspending performance with low-dosage. It is also widely used in O/W lotions and creams as a favorable suspending agent. 

 

Features and Benefits   

l Short flow properties 

l High viscosity 

l High suspending, thickening and stabilizing ability 

 

Recommended Applications 

l Hair styling gels 

l Moisturizing gels 

l Bath gels 

l Hand, body and face lotions 

l Creams

 

Formula Guidelines

l Typical recommended dosage at 0.2-1.0 wt %. 

l To disperse NM-Carbomer996 completely, it should be slowly and carefully sprinkled to dispersion medium while the mix is stirred rapidly to avoid formation of lumps; extremely high shear rate mixer should be carefully employed to avoid viscosity loss.   

l The ideal viscosity can be achieved at pH ranges of 5.0~10.0 when neutralized; In a hydoalcoholic system, a correct neutralizer must be chosen carefully based on the amount of alcohol to be gelled.    

l After neutralization, high-shear and lasting stirring should be avoided to keep stable thickening ability.    

 

Standard Packing: 20kg cardboard box with PE lining

Storage: Keep tightly closed in cool, dry and well-ventilated area 

Shelf Life: 24 months