High manganese steel x120mn12 MN13 1.3401
1.Standard: EN,GB,ASTM,DIN
2.TK:3-50mm
3.Width:1000-2500mm

 

High manganese steel x120mn12 MN13 1.3401 

Mn13(X120Mn12)is the best choice for resist-high impact ,the material of big stress in 

wear resistance.The high manganese steel have two biggest features: one is external impact 

more bigger ,the  wear-resistance of appearance is more higher ; another is with the gradually 

abrasion of densified laminated appearance, new densified laminated process is formed continually.

 

Mn13(X120Mn12)wroughtsteel plate have wonderful abrasion resistance of high impact abrasion 

and big stress abrasion, when using it will not appear crash.It also has the excellence of easy for 

cutting ,welding ,curving and other mechanical properties for process.The traditional used high 

chrome forging only have the good wear-resistance of moving abrasion. 

Mn13(X120Mn12 rolled plate is reduced the cost of useing for quick wear part of low equipment 

and save the overhaul fee of equipment,so it improves the competition.

 

1. Standard: GB, ASTM, JIS, DIN

    American standard: ASTM  A128

    Europe standard: X120Mn12

    JIS:SCMnH11

    China standard:Mn13

    ZGMn13 China cast steel

    High manganese steel

2. Brand name: Baosteel

3. Specification: TK3-200mm, Width: 500-3000mm, Length: 1000-12000mm

4. Chemical composition (%)

C1.1~1.3

Si0.3~0.5

Mn 12.0~14.0

P≤0.010

S≤0.040

Cr (1.50)

 5. Mechanical properties

Tensile Strength Rm(Mqa)    880~1130

Yield strength  Re(Mpa)   ≥410

Reduction of area A(%)   ≥40

Ballistic work  Akv(J) 124(normal temperature)

6. Payment term: TT or L/C
7. Shipment date: around one Month after confirming the deposit.

8. Packing: Steel belt packing, wooden or steel pallet.

7. Application: wear-resistance steel for scaleboard of shot-blasting machine,scaleboard of ball crusher; ball grinder,bucket lip of grab,screw die of crusher etc

Testeel could offer 

1.5/2/3/4/5*1000*2000

6-51*1500-2200*4000-6000

Welcome to have more enquiry to us.