Glass-fiber Reinforced PBT Compound

Introduction

Polyethylene terephthalate(PBT) is a kind of engineering plastics with excellent properties. It has good mechanical properties, electrical insulation, heat resistance, weatherability, chemical resistance and excellent molding properties. Modified PBT are widely used in Automobile, Electronics, Lighting, IT and Communications industries.

Characteristics of PBT resin

1.It's easy to be molded with fast crystallization. 2.With melting point around 225℃, it provides excellent heat resistance. 3.After reinforced by fiber glass, mechanical strength is increased. 4.It has low moisture absorption and excellent size stability 5.Its low friction coefficient enables good anti-abrasion property. 6.It is highly resistant to chemicals, solvents and weatherproof. 7.It offers excellent flexural property 8.With further processing, it can be upgrade to flame-retardant grade to match higher requirement. 9.With high permittivity,its electrical properties is further enhanced. 10.It can be welded by supersonic, so assembly is greatly simplified.

Application of PBT resin

1.PBT fiber 2.Optical Cable Coatings 3. PBT film 4.PBT Master Batch 5.Glass-fiber Reinforced PBT Compound 6.Flame Retardant Grade PBT Compound 7.Electronic Parts, Electrical Parts and Auto Parts.

Contact Person: Shirley

Email: business-15@nt- .com

Tel:86-513-85515677

Fax:86-513-85322299

Mobile: 86-15190879291

Grade	12-1	12-2	12-3	12-4	12-5	11-1	11-2
Intrinsic Viscosity(dl/g)	0.68±0.02	0.75±0.015	0.79±0.015	0.83±0.015	0.85±0.015	0.88±0.015	0.94±0.015
COOH Groups(meq/kg)	≤25	≤25	≤25	≤25	≤25	≤25	≤25
color L*	≥85	≥85	≥85	≥85	≥85	≥85	≥85
color b*	≤2	≤2	≤2	≤2	≤2	≤2	≤2
Melting flow Index(g/10min)@235℃	110-160	70-90	50-70	42-55	35-50	32-42	23-30
Specific Gravity	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32
Tensile Strength(kg/c㎡)	500-600	500-600	500-600	500-600	500-600	500-600	500-600
Tensile Elongation(％)	≥30	≥30	≥30	≥50	≥50	≥50	≥90
Izod Impact Strength(kg-cm/cm)	≥4.0	≥4.0	≥4.0	≥4.5	≥4.5	≥4.5	≥4.5
Dielectric Strength(kV/mm)	≥20	≥20	≥20	≥20	≥20	≥20	≥20
Melting Point(℃)	225±2	225±2	225±2	225±2	225±2	225±2	225±2
Water content(wt％)	<0.3	<0.3	<0.3	<0.3	<0.3	<0.3	<0.3

Grade	11-3	11-4	11-5	11-6	11-7	11-8	11-9
Intrinsic Viscosity(dl/g)	0.975±0.015	1.00±0.015	1.06±0.015	1.10±0.02	1.20±0.02	1.23±0.02	1.30±0.02
COOH Groups(meq/kg)	≤30	≤30	≤30	≤30	≤35	≤33-40	≤40
color L*	≥85	≥85	≥85	≥85	≥85	≥85	≥85
color b*	≤3	≤2	≤2	≤3	≤3	≤4	≤4
Melting flow Index(g/10min)@235℃	20-25	18-22	14-18	11-14	7-10	4-7	4-7
Specific Gravity	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32	1.30-1.32
Tensile Strength(kg/c㎡)	500-600	500-600	500-600	500-600	500-600	500-600	500-600
Tensile Elongation(％)	≥120	≥120	≥120	≥150	≥180	≥180	≥200
Izod Impact Strength(kg-cm/cm)	≥5.0	≥5.0	≥5.0	≥5.5	≥6.0	≥6.0	≥6.0
Dielectric Strength(kV/mm)	≥20	≥20	≥20	≥20	≥20	≥20	≥20
Melting Point(℃)	225±2	225±2	225±2	225±2	225±2	225±2	225±2
Water content(wt％)	<0.3	<0.3	<0.3	<0.3	<0.3	<0.3	<0.3