Polyethylene (PE) Self-adhesive Waterproof membrane

Model:	-
Brand:	Kailai
Origin:	Made In China
Category:	Construction & Decoration / Waterproof Materials
Label:	PEwaterproof membrae , waterproof sheet , PE membrane
Price:	-
Min. Order:	-

Inquire Now

Product Description

1.Description

Polyethylene (PCV) Self-adhesive Waterproof membrane is a new polymer waterproof membrane which is made from secov polymer sheet which coated with non asphalt self-adhesive compound membrane,processed into the Environment-friendly and self adhesive polymer waterproof membrane.

Classified by material:

Type	Width(m)	Thickness(mm)
EVA	2.00 or customized	0.7,1.2,1.5
ECB
HDPE
LDPE

2.Feature

One waterproofing ,two proofing,the waterproofing is more reliability
High tensile strength, good elongation and dimensional stability.
Waterproofing performance will not be effected by major structural settlement,ground water seepage could be prevented effectively.
Excellent aging resistance,long lifetime,no pollution.
Welding installation. Joints are solid and environment friendly,
-25℃ has good flexibility.
The surface could reflect ultraviolet irradiation,low temperature.
Good plasticity, easy and suitable for details installation.

3.Technical Index

NO	Test Item		Technical Index
1	Pull(N/50mm) ≧		800
2	Membrane elongation at break,% ≧		450
3	Nail tear resistance / N ≧		500
4	Tear resistance, N/mm ≧		60
5	Impact property		Diameter(10±0.1)mm,no leakage
6	Static loads		20kg,no leakage
7	Heat resistance		70 ℃,2h,no displacement,no flowing,no dripping
8	Cold bending		-25℃ no crack
9	Anti-fluid-water		0.6Mpa,no leakage
10	Peeling strength with Post pouring concrete, N/mm	No treament	2
		Surface contaminated by cement	1.5
		Surface contaminated by sediment	1.5
		Ultraviolet aging	1.5
		Thermal ageing	1.5
11	Peeling strength with Post pouring concrete wetting, N/mm		1.5
12	Mechanical property on joint	shear strength N/50mm ≧	500 or specimens damage
12	Mechanical property on joint	Peeling strength N/mm ≧	1.2
13	Alkali resistance( saturation Ca(OH)2 solution, Room tp168h)	strength retention % ≧	90
		elongation retention % ≧	80
		Cold bending	-25℃, no crack
14	Thermal ageing(70℃,168h)	strength retention % ≧	90
		elongation retention % ≧	80
		Cold bending	-18℃, no crack