~Boao artificial cladding wall Montecarlo stone are made of white cement, shale ceramisite, BYER pigment, sand and other aggregate materials. After years of accumulative experience, we have developed more than 196 kinds of stone veneer by now. Each sort of stone veneer has their relevant corner to make the entire wall keep as an accordant looking.

~Advantage Of Boao Artificial Montecarlo Stone

Bo'ao artificial faux montecarlo stone widely used as exterior and interior veneers in villas, apartments, vacation,homes, hotels, parks, golf yards, pubs, café Bars, entertainment concourses, residential halls and so on.

1. High quality, natural color and delicate texture, solid surface.
2. Light weight, only 1/2 or 1/3 the weight of natural stone
3. Hundreds of colors can be customized.
4. Installation is quicker, easier and cheaper
5. Environmental friendly, odor-free,radiation-free,non-toxic,heat-insulation,non-radioactive.
6. Durable and unlikely to rust, piebald or fade. Resistance to fracture and impact. Fire retardant. Sound insulation, dampness penetration.
7. Virtually maintenance free
8. Energy saving comparing to the natural stone.

~Testing report of Boao Faux Montecarlo Stone Veneer

 

MATERIALS:

-cement   GB/T2015 requirements

-shale ceramisite   GB/T2840 requirements    

-pigment   GB/T1865, purchase from BAIER

_______________________________________________________________________________

 

--Appearance

Visual inspection according to the standard sample. Color testing is in accordance with GB/T1865.

 

--Water absorption

In accordance with GB/T9966.3.

 

--Flexural strength

In accordance with GB/T3810.4, test 10 pieces, sample 160*40*20(mm).

 

--Resistance to freezing and thawing

5 pieces, soak for 24h, then put them into the cryogenic box with the temperature -15℃±2℃; then put them into the water of 10℃ for 2h. Recycle the process for 50 times.

 

--Resistance to artificial aging

In accordance with GB/T1856 and test for 250h.

 

--Volume density

In accordance with GB/T9966.3.

 

--Resistance to chemical corrosion

In accordance with GB/T3810.13, Low concentration acid solution test.

 

--Radioactivity

In accordance with GB/T655, internal exposure index less than 0.6Bq/Kg, external exposure index less than 0.8Bq/Kg.