Industrial Belt

Special CR treated outer jacketing fabric for higher durability

 

Product Description

Features

Special CR treated outer jacketing fabric for higher durability

Anti-static, oil & heat resistant

Maximum Belt linear speed (Classical section: up to 30 m/sec, Wedge section: up to 42 m/sec, Narrow section: up to 45 m/sec)

Temperature range: -18°C to +80°C

ATEX certified FRAS Belts are also available

Constructional Details

Wear-resistant bias-cut neoprene rubberised polyester cotton fabric

High tensile cord embedding cushion rubber compound

High tenacity, low stretch, specially treated polyester cords

Especially compounded high modulus compression rubber

We are Industrial Belts Supplier.

 

Product Specifications

Section	Top Width (mm)	Thickness (mm)	Angle (Degree)	Min. Pulley Dia. (mm)	Manufacturing Range		Belt Length Factor (mm)			Length Desg.
					Min. (inch / mm)	Max. (inch / mm)	Lp to La	Li to Lp	Li to La
Classical Section
Z	10	6	40	50	40 / 1000	590 / 15000	16	22	38	Li
A	13	8	40	71	40 / 1000	590 / 15000	14	36	50	Li
B	17	11	40	112	40 / 1000	590 / 15000	26	43	69	Li
C	22	14	40	180	40 / 1000	590 / 15000	32	56	88	Li
D	32	19	40	355	40 / 1000	590 / 15000	40	79	119	Li
E	38	23	40	500	40 / 1000	590 / 15000	53	92	145	Li
Wedge Section
SPZ	10	8	40	63	40 / 1000	590 / 15000	13	37	50	Lp
SPA	13	10	40	90	40 / 1000	590 / 15000	18	45	63	Lp
SPB	17	14	40	140	40 / 1000	590 / 15000	28	60	88	Lp
SPC	22	18	40	224	40 / 1000	590 / 15000	30	83	113	Lp
Narrow Section
3V	9.7	8	40	63	40 / 1000	590 / 15000	13	37	50	La
5V	15.8	14	40	140	40 / 1000	590 / 15000	25	60	85	La
8V	25.4	23	40	335	40 / 1000	590 / 15000	53	92	145	La

 

ZX AX BX CX

Classical Raw Edge Cogged V-Belts

Moulded Raw Edge Cogged Belts, as the name implies do not have textile wrapping on the outer surface. These are produced by slitting individual belts from rubber sleeve and hence they are called as Cut edge belts.

The manufacturing methods also make it simpler to produce belts with cogs underside thereby reducing the bending resistance of the belts and allowing them to operate on pulleys with approximately 20% smaller diameters. The decreased bending resistance reduces mechanical losses during bending and leads to improved efficiency and reduced working temperature. Heat dissipation is further improved by the larger area between the belt and the surrounding atmosphere and also by the air turbulence around the cogs during operation. Multi stage drives can be eliminated. These belts require a higher tension than the wrap belts so as to exhibit higher power transmission capability.

 

Features

•  Special top layer with fabric

• Tough tensile member for greater strength

• Molded Cogs

• Polychloroprene cushion rubber compound

• Fiber filled polychloroprene base compound

• Speed ratios up to 1:12 are possible: This eliminates the need formulti stage drives

• Temperature range: -18oC to +100oC

• Maximum recommended belt speed is 30 m/s*

• Antistatic, oil and heat resistant

 

Advantages

The advantages of Raw Edge Moulded Cogged Belts over Wrap Belts are of great importance in following cases-

1. Drives with very small pulley diameters

2. High ambient temperatures

3. High belt speeds

4. High level of power transmission

 

Applications

It is recommended to use these belts in borderline cases if difficulties are anticipated in using wrap construction belts

Primarily used as replacement on industrial drives. The classical belts are recommended in special applications such as V-flat drives. In the same manner these belts are advantages where reverse idlers have to be used, because of smaller heights.

 

Standards & Dimension:

Section	Top Width	Thickness	Angle	Manufacturing Length Range
	(mm)	(mm)	(Deg)	Min. (inch/mm)	Max. (inch/mm)
ZX	10	6	40	40 / 1000	196 / 5000
AX	13	8	40	40 / 1000	196 / 5000
BX	17	11	40	40 / 1000	196 / 5000
CX	22	14	40	40 / 1000	193 / 5000

More information please click here.