Model: | 1.4545 |
---|---|
Brand: | Fushun |
Origin: | Made In China |
Category: | Metallurgy , Mining & Energy / Metallurgy & Mining / Stainless Steel |
Label: | 1.4545 , UNS S15500 , 15-5PH |
Price: |
US $2000
/ ton
|
Min. Order: | 1 ton |
Introduction:
15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good
corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the
aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.
Applications:
Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears
Quality Standard:
ASTM A564 2004 Standard Specification for Hot Rolled and Cold Finished Age Hardening Stainless Steel Bars and Shapes
ASTM A705 Standard Specification for Age Hardening Stainless Steel Forgings
All Grades Comparison
DIN:1.4545
ASTM:XM-12
UNS:S15500
CNU:15-5PH
Chemical Composition(%)
C:0.07max,Si:1.0max, Mn:1.0max, P:0.030max, S:0.035max, Cr:14.0-15.0, Ni:3.5-5.5, Cu:2.5-4.5, Nb+Ta:0.15-0.45
Mechanical Properties
Delivery Condition:A(annealed)
Hardness (HRC):35 max
Delivery Condition:H 900
Modulus of Elasticity(GPa):197.6
Modulus of Rigidity(GPa):77.3
Tensile Strength Rm (Mpa):1378min
Yield Strength Rp0.2 (Mpa):1276min
Elongation % in 2″ (50.8 mm):14min
Reduction Of Area (%):50min
Hardness (HRC):44min
Delivery Condition:H925
Tensile Strength Rm (Mpa):1309min
Yield Strength Rp0.2 (Mpa):1207min
Elongation % in 2″ (50.8 mm):14min
Reduction Of Area (%):54min
Hardness (HRC):42min
Delivery Condition:H1025
Modulus of Rigidity(GPa):75.9
Tensile Strength Rm (Mpa):1173min
Yield Strength Rp0.2 (Mpa):1138min
Elongation % in 2″ (50.8 mm):15min
Reduction Of Area (%):56min
Hardness (HRC):38min
Delivery Condition:H1075
Modulus of Rigidity(GPa):69
Tensile Strength Rm (Mpa):1138min
Yield Strength Rp0.2 (Mpa):1035min
Elongation % in 2″ (50.8 mm):16min
Reduction Of Area (%):58min
Hardness (HRC):36min
Delivery Condition:H1100
Tensile Strength Rm (Mpa):1035min
Yield Strength Rp0.2 (Mpa):931min
Elongation % in 2″ (50.8 mm):17min
Reduction Of Area (%):58min
Hardness (HRC):34min
Delivery Condition:H1150
Modulus of Rigidity(GPa):69
Tensile Strength Rm (Mpa):1000min
Yield Strength Rp0.2 (Mpa):862min
Elongation % in 2″ (50.8 mm):19min
Reduction Of Area (%):60min
Hardness (HRC):33min
Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.