Powder metallurgy bearings in tin bronze powder as raw material, mold pressing after sintering in high temperature plastic.Its matrix are small, uniform pore, after oil dipping formation oil state.Use of low cost, are widely used in household electric machinery, textile machinery, chemical machinery, automobile industry and other fields.
JDB - 650 Mosaic solid self-lubricating bearings: belongs to a series of sliding bearing, is in the high force brass (main chemical composition Cu Al Mn Fe Ni zinc percentage respectively: 60 ~ 66% 5.0 0.2 2.5 ~ 2.5 ~ 7.5% and 5.0% ~ 7.5% ~ 0.5% 22 ~ 28%) on the base of inlaid graphite or a high-performance solid lubrication MoS2 solid lubricant products.It broke through the general bearing on the limitations of the oil film lubrication.In use process, through the friction heat make solid lubrication and shaft friction, the excellent conditions of forming, powder and oil lubrication, both to protect shaft wear and tear, and the solid lubrication characteristics of eternity.It is twice as tall as general copper sleeve, wear-resisting performance is twice as high.
It is recommended to use occasions:
Now the product has been used in metallurgical continuous casting machine, train bracket, steel rolling equipment, mining machinery, shipping, steam turbine and other high temperature, high load, etc of low speed and heavy loading.
Technical parameters:
Substrate material: CuZn25A16Fe3Mn3
Dynamic load limit: 100 n/mm ^ 2
Basic hardness: HB210 ~ 270
The friction coefficient of mu: < 0.16
Temperature: 300 ℃
Dry sliding speed: 0.4 m/s oil 5 m/s