~Ingredients: incorporated copolymer of Vinylidene fluorideand hexafluoropropylene(HFP), containing curing system and various additives and filler
 
Characteristics:proprietary curing agent compounding technology, excellent processing, mold release, mold flow and compression set properties
 
Processing: compression molding, transfer molding and injection molding; suitable for producing complicated sealing products, especially for O-rings products.
 
Curing system:Bisphenol
 
Data:
Fluorine Content: 66%
Gravity: 1.95 g/cm3
Color: Black or any other color
Solubility: LMW ketones or esters
Typical Rheological Properties:
Monsanto Moving Die Rheometer[MDR2000®] 100cpm, 0.5°Arc,6 minutes@177°C
ts2[Time to 2 inch-lb rise from minimum]: 1′22″
t90[Time to 90% cure]: 2′35″

Typical Physical Properties:
Press Cure 10 minutes@170°C
Post Cure 24 hours@230°C
Tensile Strength[ASTM D412]: 14 MPa
Elongation at break[ASTM D412]: 210%
Hardness Shore A[ASTM D 2240): 70
Compression set[ASTM D395 Method B,24h@200°C]: 15%