Direct Roving for LFT

Model:	362J
Brand:	Jushi
Origin:	Made In China
Category:	Construction & Decoration / Other Construction Materials
Label:	Direct Roving LFT , E-glass Fiberglass , Jushi Fiberglass
Price:	US $0.5 / kg
Min. Order:	1000 kg

Inquire Now

Product Description

Direct Roving for LFT
Direct Roving for LFT is coated with a silane-based sizing compatible with PA, PBT, PET, PP, ABS, PPS and POM resins. It is widely used in industries of automotive, electromechanical, home appliance, building & construction, electronic & electrical, and aerospace.

Direct Roving 362J for LFT
362J Direct Roving is specially designed for long fiber-glass thermoplastic(LFT),process and compatible with modified PP resin. 362J is designed for LFT-D(Long Fiberglass Reinforced Thermoplastics Direct / In-Line Compounding),LFT-G(granulate) process and widely used in automotive, construction, sports, electric and electronic applications.

Specifications	Features	Technical Parameters
Type of Glass: E-Glass (E)	• Good dispersion • Good abrasion resistance and low fuzz • Good compatibility with PP resin • Excellent mechanical properties of the finished composite product	Linear Density (%): ± 5 ISO1889
Type of Fiberglass: Direct Roving (DR)
		Moisture Content ≤ 0.10% ISO 3344
Standard Linear Mass Densities 400,600,1200,2400,3000 (Tex)
	Resin Compatibility • PP
Filament Diameter: 16,17,19 microns		Size Content (%): 0.55 ± 0.15 ISO 1887
	Uses • Automotive • Construction • Electrical & electronic applications • Sports apparatus
Size Code: EDR17-2400-362J
		Breakage Strength (N/tex): ≥ 0.30 ISO 3341

LFT-D Process
LFT-D (Long Fiber Thermoplastic – Direct) includes three variants: Direct Injection, Direct Pultrusion and Direct Compression Molding. In this process, Polymer pellets, additives and glass rovings are all introduced into a twin-screw extruder where the polymer is melted and compound formed. Then, the molten compound is immediately, directly molded into the final part.

LFT-G (or LGT-P) Process

In the LFT-G (or LGT-P) process, the resin is heated together with additives to a molten phase and pumped to the die-head. The continuous roving is pulled through dispersion die, ensuring good impregnation of the glass fibers by molten polymer and consolidation into a rod. After cooling, the rod is chopped into reinforced pellets of 12-25 mm length. The end-users can use injection or compression molding to make final parts with well defined properties.including Compression and Injection Molding. It is used in automotive, electrical & electronics, aerospace and defense applications.