Hydroxypropyl Methyl Cellulose

 

 

 

PRODUCT INTRODUCTION

 

HPMC are types of non-ionic cellulose ether, which are a powder of white to off white color, that function as a thickener, binder, film-former, surfactant, protective colloid, lubricant, emulsifier and suspension and water retention aid. In addition, there types of cellulose ethers exhibit properties of thermal gelation, metabolic inertness, enzyme resistance, low odor and taste, and PH stability. 

Due to the myriad of properties, HPMC is often used to substitute many other additives with lower concentration, making HPMC an incredibly efficient and effective additive in area of adhesives, construction, foods, household products, pharmaceuticals, and etc.

PHYSICAL AND CHEMICAL PROPERTIES

 

* Particle size: 98.5% passes through 100 mesh; 100% passes through 80 mesh.

* Charring temperature: 280-300℃.

* Bulk density: 0.25-0.70 g/cm3 (Usually around 0.5 g/cm3 )

* Real specific gravity: 1.26-1.31.

* Browning temperature: 190-200℃.

* Surface tension: (2% water solution) 42-56dyn.cm.

* Properties: Dissolved in water and some organic solvent such as ethanol. propyl alcohol. ethylene chloride, the water solution is of surface activity. It is a nonionic surface active agent. Gelation temperature is different for different grades. For example, among 60RT Hydroxypropyl Methylcellulose, 60 is gelation temperature, Namely, 2% water solution will form gelation at 60%.

 

TECHNICAL DATA SHEET

 

 

PRODUCT DESCRIPTION

 

[ STORAGE ] Sealed and kept in a dry place

[ PACKAGE ]Woven polypropylene bag

[ NET WEIGHT ] 25kg / bag

 

Application

 

1. Tile Adhesives

A.High water retention  B.Excellent sag resistance  C.Good workability

 

D.Good adhesive strength  E.Long open time  F.Easy mixing

 

 

 

 

2.EIFS

A. Improved adhesion strength   B.Good wetting ability

C.High water retention      D. Long open time

 

 

3.Gypsum based plaster

A. High pumpability   B.High sag resistance   C.Good workability

D. High water retention  E.Good adhesive strength   F.Good spreadablity

 

 

4.Joint Filler

A.High water retention B.Easy working ability C.Strong adhesion

D.Good consistance E.Reducing whiskering F.Strong sag resistance

 

 

5.Masonry Mortars

A.Good adhesive B.Good workability C.High compressive strength

D.High water retention E.Effcient Thickening F.Crack resistance

 

 

6.Putty

A. High water retention B. Good Workability C.Crack Resistance

D.Good consistance E.Cost Effective F.Good spreadability

 

 

7.self-leveling compound

A. Good adhesive strength  B.Smooth surface  C.Good leveling

D. High water retention  E.Crack resistance  F.Excellent stability

 

 

 

8.Cement based plaster 

 

A. High water retention  B.Good workability  C. Crack resistance       

D. Excellent sag resistance    E. Long open time     F. Easy spreading