Material: Monel /Monel brand: K500

 

Tensile strength Mpa:896.3-- 1137.6 Yield strength Mpa:586-- 872

 

Elongation (%) : 20%-- 35% Hardness: 33±1.5

 

Density: 0.3051 BS /cubic inch Near-roundness mm/Ball Roundness:≤0.002

 

Accuracy grade: GB100

 

Nickel content as high as 63%~70% of ordinary stainless steel about 10 times, strong corrosion resistance.

 

 

 

Common specifications: 4mm, 4.7625mm, 5.0mm, 5.556mm, 6.35mm, 7.938mm, 9.525mm, 14.288mm

 

 

 

Characteristics: K500 Monel alloy ball has corrosion resistance, cavitation resistance, low temperature fission resistance, high sealing, no magnetic and other excellent mechanical properties and the alloy has no plastic-brittle transition temperature, so it is very suitable for a variety of low temperature equipment. The alloy has excellent corrosion resistance in solid and gaseous media, and excellent corrosion resistance to concentrated metal. It is also resistant to corrosion of neutral solution, water, sea water, atmosphere and organic compounds. An important characteristic of the alloy is that stress corrosion cracks do not occur.

 

 

 

Application: Often used in blowdown valve, check valve, grease valve and working parts in high corrosive environment with good sealing performance.

 

 

 

Hastelloy alloy:

 

Face-centered cubic structure, strong corrosion resistance, especially resistance to hydrogen chloride, chlorine and hypochlorous acid corrosion, chlor-alkali industrial equipment using Hastelloy alloy.

 

Hastelloy alloy common grade: Hastelloy C,Hastelloy c-4, Hastelloy c-22, Hastelloy C-59, Hastelloy c-276, Hastelloy C-2000, Hastelloy B, Hastelloy B-2, Hastelloy B-3, Hastelloy G-30, Hastelloy G35, baiHastelloy X, Hastelloy 188, HastelloyR-135, HastelloyH-2

 

 

 

Hastelloy alloy material is mainly resistant to wet chlorine Du, various oxidizing chlorides, zhi chloride solution, sulfuric acid and oxidizing salt. Dao has good corrosion resistance in low temperature and medium temperature yan acid. Therefore, in the past 30 years, in harsh corrosive environment, such as chemical, petrochemical, flue gas desulfurization, pulp and paper, environmental protection and other industrial fields have a quite wide range of applications.

 

 

 

The alloy has the following characteristics: ① It has excellent corrosion resistance to most corrosive media in oxidation and reduction atmosphere. ② It has excellent pitting corrosion resistance, crevice corrosion and stress corrosion resistance. The high content of Mo and Cr makes the alloy resistant to chloride ion corrosion, and the W element further improves the corrosion resistance. At the same time, Hastelloy C-276 alloy is one of the only corrosion resistant materials to wet as, hypochlorite and chlorine dioxide solution, and has significant corrosion resistance to high concentration of salt chloride solution such as ferric chloride and copper chloride. Suitable for all concentrations of sulfuric acid solution, is one of the few materials can be applied to hot concentrated sulfuric acid solution. Application: petrochemical equipment, heat exchanger, flue gas desulfurization equipment, fluid chemical pump, fluorine chemical, etc

 

 

 

Company is set

 

Product name: Starley alloy ball

 

Material: Stellite metal brand: Stellite 20 / CO120

 

Ingredient: Co, Cr, W, C

 

Hardness: HRc54 ~ 59

 

Melting temperature: 1260-1265℃

 

Ultimate compressive strength: 1637MPa

 

Product common specifications: φ6.35, φ7.9375, φ10, φ12.7, φ14.28, φ19.05, φ22.225, φ25.4, φ28.575, φ30.15, φ34.93, φ38.1, φ41.3, φ50.8

 

Product performance: high temperature resistance, wear resistance, cavitation resistance, corrosion resistance. The wear resistance at high temperature is far superior to other metals, and can still maintain a comparable hardness value.

 

Product application field:

 

It is suitable for mechanical parts with high speed operation, large amount of heat or corrosive gas around. The anti - abrasion and anti - bite properties of Starley alloy ball are extremely superior when used as sealing surfaces of valves and valves. (Mainly used for export, valve factory, power plant, bearing plant, machinery factory, oil field mining equipment and so on.)

 

 

 

Inconel alloy

 

Product name: Inconel625/UNS N06625

 

General international BAI names are Inconel Alloy 625, NS336, NAS 625, W.N.R.2.4856, UNS NO6625, Nicrofer S 6020-FM 625, and ATI 625

 

Executive standard: duASTM B443/ASME SB-443, ASTM B444/ASME SB-444, ASTM B366/ASME SB-366, ASTM B446/ASME SB-446, ASTM B564/ASME SB-564

 

 

 

Main components: Carbon (C) 0.01 or less, manganese (Mn) of 0.50 or less, nickel (Ni) or greater dao58, silicon (Si) of 0.50 or less phosphorus (P) of 0.015 or less, sulfur (S) of 0.015 or less, chromium (Cr) 20.0 ~ 23.0, iron (Fe) of 5.0 or less, aluminum (Al) of 0.4 or less, titanium (Ti) of 0.4 or less, niobium (Nb) 3.15 ~ 4.15, Cobalt (Co) ≤1.0, Molybdenum (Mo)8.0 ~ 10.0

 

Physical properties: 625 Alloy density: 8.44g/cm3, melting point: 1290-1350 ℃, magnetism: none

 

Heat treatment: keep the temperature between 950-1150℃ for 1-2 hours, fast air cooling or water cooling.

 

Mechanical properties: tensile strength: σb≥758Mpa, yield strength σ B ≥379Mpa, elongation: δ≥30%, hardness :HB150-220

 

Corrosion resistance and main operating environment:

 

INCONEL 625 is an austenitic superheat resisting alloy with nickel as the main component. Due to the strengthening effect of molybdenum and niobium solid solution contained in nickel chromium alloy, it has ultra-high strength and extraordinary anti-fatigue characteristics at low temperature to 1093℃, and is widely used in aviation industry. Although the alloy is designed to adapt to the strength of high temperature environment, the high content of chromium and molybdenum alloy has high resistance to corrosion spots and fission corrosion of many corrosive media, from high oxidation environment to general corrosion environment, showing excellent corrosion resistance. INCONEL 625 also has superior corrosion resistance against chlorine-contaminated media such as seawater, geothermal water, neutral salts and saltwater.