Silicon Carbdie Bricks for waste incineration plant

Silicon Carbdie Brick for waste incineration plant is an advanced high-grade refractory material. The products mainly includes radiant tube, brick, and deformed parts, etc. With the advantages of energy saving, environmental protection, high-temperature resistance, high corrosion resistance, and so on, Si3N4 Bonded SiC products can be widely used in the field of steel, non-ferrous, chemical construction materials,etc.

Performance

1. Hard texture, the Moh’s hardness is about 9, be second only to diamond, belongs to hard material in non-metallic material field;

2. Superior strength in normal temperature, as well as it under 1200-1400℃. The maximum service temperature can be reached up to 1650-1750℃ for the environment is different.

3. Small thermal expansion.SiC products with the advantages of high thermal conductivity and hard to produce thermal stress, compare SiC products with Si3N4 Bonded SiC products, the latter maintains high thermal shock resistance, long service life. As Si3N4 Bonded SiC with the features of strong creep-resistance in high temperature, high corrosion resistance, extremely cold or hot resistance, and antioxidant, it can be made into products which with high dimensional accuracy easily.

 

Application

Widely used in the field of steel, non-ferrous, chemical construction materials, and other industries. These products maintains the characters of energy saving, environmental protection, and cost reduction.

 

Silicon Carbdie Bricks for waste incineration plant

The shape of bricks used in wasteincinerator is more complex. The garbageincineration power generation projects are fixed in the heat pipe brick with ceramic bolts, pipe dynamic water. Using silicon nitride bonded silicon carbide to conduct high heat conduction, the heat generated by garbageincineration is transmitted to the heating water of the pipe to generate electricity. The corrosion and oxidation resistance of silicon nitride bonded silicon carbide is used to deal with a lot of corrosive and strong oxidizing gases generated by garbageincineration.

 

These products are obtained by reaction sintering of a mix of SiC with Si fines and additives and nitridation in N2 atmosphere at~1450℃

 

The following reaction would take place:

3Si+2N2→Si3N4

3Si+SiO2+2N2→2Si2N2O

Si3N4+SiO2→2Si2N2O

Si3N4  Si2N2O act as binder for the SiC grains

 

 

Item	Value
Bulk Density	≧2.65   g/cm3
Apparent porosity	≦15     %
Compressive strength	≧150    MPa
Rupture strength at r. t.	≧40     MPa
SiC	≧75     %
Si3N4+Si2N2O	≧15     %

 

 