SST Multilayer Zirconia Blocks

HaHasmile® SST Multilayer zirconia block dental lab CAD CAM zirconia block is multilayer zirconia, SST Multilayer zirconia blocks with higher translucency and low strength, it suitable for making anterior bridge and crown, HaHasmile® SST Multilayer zirconia block is color gradient multilayer zirconia blocks.

 

HaHasmile® SST Multilayer Zirconia Blocks Features:

6 layers gradient multilayer colors

Bending strength 860Mpa;

Higher translucent 45%;

 

It is more translucency than ST+Multilayer zirconia block;

Suitable for anterior crown and bridges, Inlay, Onlay, posterior crown and bridge;

HaHasmile® SST Multilayer Zirconia Block is Multilayer zirconia block.

Available for 98mm / 95mm / AG / Sirona

Thickness: 12mm / 14mm / 16mm / 18mm / 20mm / 22mm / 25mm

Color: A1 A2 A3 A3.5 B1 B2 B3 C1 C2 D2

 

HaHasmile® SST Multilayer zirconia blocks are produced by CIP technology and pre-sintered in low temperature. Although the product has some strength, because of porosity, please handle carefully.

 

Chemical Composition

Components

SST Multilayer Zirconia block

Nanometer zirconia powder

≥98%

CeO₂

0.5%

Fe2O3

0.5%

Er2O3

0.5%

Other Oxides

0.5%

 

SST Multilayer zirconia block Mechanical Property

Sintered Density g/cm³

>6.02g/cm³

Bending Strength Mpa

≥860Mpa

Translucency

45%

Hardness(Hv10)

1250MPa

Sintered temperature(°C)

1500°C

Radioactivity Bq.g-1

<0.1

Cytotoxicity

Level0

 

Indications:

Coping, coping bridge, full arch coping bridge, custom abutment, abutment screw retained bridge, inlay,onlay, posterior crown, posterior crown bridge,full arch crown bridge.

 

Application Method

Coping

Scanning and Designing — Milling — Cleaning — Sintering — Polishing — Porcelain — Staining — Finishing

 

Full contour crown

Scanning and Designing — Milling — Cleaning — Sintering — Polishing — Staining — Finishing

 

HaHasmile® SST Multilayer Zirconia Block Sintering Curve:

1-6 units bridge(10h)

Start temp

Heating rate

Maximum temp

Heating rate

Maximum temp

Holding time

Heating rate

Maximum temp

Holding time

Cooling rate

Cooling to

Cooling rate

Cooling to

Room temp

12°C/min

1100°C

1.2°C/min

1400°C

10min

2°C/min

1500°C

120min

8.5°C/min

900°C

Natural

100°C

 

Other information you can also visit:

http://www.weblogworld.com

http://www.kjsmachcnc.es

http://www.textoblog.com

http://www.blogequipment.com

http://www.manufacturerblogger.com

http://www.infoblogdirect.com

http://www.weblatestnews.com

http://www.blog4evers.com

http://www.moreinformationblog.com

http://www.webmedicalblog.com

http://www.machblogger.ltd

Payment Terms:T/T,paypal
SST Multilayer Zirconia Blocks 1

Member Information

HaHasmile®
Country/Region:Hu Nan - China
Business Nature:Manufacturer
Phone:17872373128
Contact:Cindy Wu (sales manager)
Last Online:01 Sep, 2021