TBL-8900~8980 Liquid Silicone Rubber

 

• Product Description:

This series product is two-component addition liquid silicone rubber, which has high transparency, high tear strength and excellent tensile property. It formulated to meet the requirements of FDA 21CFR 177-2600 and is widely used on manufacturing of food grade products, such as infant product, sport goods, kitchen appliances, etc.

 

• Product Features:

▪ High Transparency

▪ High strength

▪ Yellowing resistance

▪ Fast molding speed

▪ Formulated to meet the requirements of US FDA 21CFR 177-2600/ROHS/REACH/LFGB

 

 

• Main Technical Parameters：

Item&Model	TBL-8920	TBL-8930	TBL-8940	TBL-8950	TBL-8960	TBL-8970
Proportion	1:1	1:1	1:1	1:1	1:1	1:1
Appearance	Transparent	Transparent	Transparent	Transparent	Transparent	Transparent
Viscosity/ mPa.s	40×104	70×104	80×104	90×104	100×104	120×104
Hardness /Shore A	18-22	28-32	38-42	48-52	58-62	63-67
Tensile Strength/MPa	≥5.0	≥7.5	≥8.5	≥8.5	≥8.0	≥8.0
Elongation/%	≥700	≥700	≥600	≥500	≥400	≥300
Tear Strength /kN/m	≥8	≥18	≥25	≥30	≥30	≥30
Specific Gravity/g/cm3	1.09	1.10	1.11	1.12	1.13	1.13
Molding Condition: 130°C X 5Min
Above data are for reference only. Factory quality inspection report shall prevail for latest testing standard and data.

• How To Use：

• S est that the consumer use the liquid injection molding machine to inject into the mold and manufacture products.
• The two components of A and B must be completely mixed by machine according to the weight or volume ratio of 1:1. The vulcanization time is determined by the molding temperature. At high temperature conditions, a short time is required for product forming. If the silicone product is thick and large, it takes longer time to mold. After vulcanization, the mold can be disassembled.

3. If the machine is shut down for a long time (more than two days), either inject component A or component B into the mixing section alone. Or remove the static mixer of the injection molding machine immediately, seal and store it in a low temperature (< 1℃) environment, or clean up the remaining rubber.

 

• Packaging, Storage and Caution:

1. This series of product is packed in 20 kg/plastic straight pail or 200 kg/metal drum, with plastic liners.

2. Products should be stored in sealed condition, kept it in a cool place and avoid rain and sun exposure.

3. This series of products are non-dangerous goods. The valid period is 1 year. If the products exceed the storage life, it can be re-tested to prove the curing speed is acceptable, if so, it can be used.

4.To prevent cure inhibition, try to avoid contact with tin compound (most condensation silicone contain tin compound catalyst) amines, sulfur and phosphorus compounds and some metal salts.

5. In this series, component A contains catalyst and component B contains cross-linking agent. When products from different manufacturers are used, tests shall be carried out to avoid cross-linking reaction.

 

Ø Liability Limitation:

The information contained herein is offered in good faith and is believed to be accurate. However, because conditions and methods of use of our products are beyond our control, this information should not be used in substitution for customer’s tests to ensure our products are safe, effective, and fully satisfactory for its intended end use. S estions of use shall not be taken as inducements to infringe any patents.

Tian Bao Li’s sole warranty is that our products will meet the sales specifications in effect at the time of shipment.

Your exclusive remedy for breach of such warranty is limited to refund of purchase price or replacement of any product shown to be other than as warranted.

To the fullest extent permitted by applicable law, Tian Bao Li specifically disclaims any other express or implied warranty of fitness for a particular purpose or merchantability.

Tian Bao Li disclaims liability for any incidental or consequential damages.