Nitronic 60 parts are CNC processed differently from other Nitronic alloy parts because of the material's excellent resistance to wear (i.e. wear caused by local adhesion and subsequent tearing of material fragments when parts slide against each other). In addition to resistance to wear and tear, the Nitronic 60 has nearly twice the yield strength of more common stainless steels such as 316 or 18-8. Nitronic 60 also has far better corrosion resistance than most similar metals. These characteristics make it ideal for mechanical parts such as shafts, fasteners or gears that experience sliding contact and require high strength when subjected to corrosive operating environments.

application
Infrastructure bridge pin and hanger expansion joint, parking deck expansion joint wear plate.
Hydraulic power generation - valve stem, gate wear ring
Oil and Gas production -- Pump wear rings, bushings, valve internals, seals, fittings, logging equipment and screens.
Food processing and pharmaceuticals - Anti-wear applications in sanitary equipment where lubricants cannot be used
Chemical and petrochemical -- Process stem, seat and valve internals, pump wear ring.

Chemical composition (wt %)
Carbon: ≤0.10 Silicon: 3.5-4.5
Chromium: 16.0-18.0 Phosphorus: ≤0.060
Nickel: 8.0-9.0 Sulfur: ≤0.030
Manganese: 7.0-9.0 Nitrogen: 0.08 ~ 0.18
Physical properties of Nitronic 60
Density, 3:0.275 pounds per inch
Modulus of elasticity, psi: 26.2 x 10 6
Coefficient of thermal expansion, 68-212˚F, /˚F: 8.8 x 10-6
Thermal conductivity, Btu/fthr˚F: 9
Specific heat, Btu /lb˚F: 0.12
Resistivity, Microhm-in: 28.7
Nitronic 60 Mechanical properties
Mechanical properties of annealed products as specified in ASTM A276
Yield strength (KSI) :≥50
Tensile strength (KSI) :≥95
Elongation (%) :≥35