1) S-BM (H)(Hand lay-up type FRP surface tissue)
Hand lay-up type FRP surfacing tissue is mainly applied in the production of hand lay-up FRP products. It has the advantages of good pattern fitness and quick resin permeating. It is characterized as covering up the texture of layers, making the surface smooth and improving the service life.
|
Item
|
Unit
|
Type
|
|
S-BM(H)-20
|
S-BM(H)-30
|
S-BM(H)-40
|
S-BM(H)-50
|
S-BM(H)-60
|
|
Monofilament Diameter
|
µm
|
9 13
|
|
Area Weight
|
g/m2
|
20
|
30
|
40
|
50
|
60
|
|
Binder Content
|
%
|
5-8
|
|
Penetrating time(two layers)
|
S
|
=<8
|
=<10
|
=<15
|
=<20
|
=<25
|
|
Tensile Strength MD
|
N/50mm
|
>=35
|
>=40
|
>=50
|
>=60
|
>=70
|
|
Moisture content
|
%
|
<0.2
|
|
Width
|
mm
|
The mat`s width will be produced according to the customers` requirements.
|
2) S-BM(W) (Wrap type FRP surface tissue)
The wrap type FRP surfacing tissue is mainly suitable for wrapping FRP pipes and vessels. It has absorbed a great deal of resin and the defendable layer has been formed at the FRP product surface. It is capable of significantly improving the performances of surface layer to realize longer lifetime and resistance against corrosion,leakage and compression.
|
Item
|
Unit
|
ype
|
|
S-BM(W)-20
|
S-BM(W)-30
|
S-BM(W)-40
|
S-BM(W)-50
|
S-BM(W)-60
|
|
Monofilament Diameter
|
µm
|
9 12
|
|
Area Weight
|
g/m2
|
20
|
30
|
40
|
50
|
60
|
|
Binder Content
|
%
|
6-9
|
|
Penetrating time(two layers)
|
S
|
=<8
|
=<10
|
=<15
|
=<20
|
=<25
|
|
Tensile Strength MD
|
N/50mm
|
>=35
|
>=40
|
>=50
|
>=60
|
>=70
|
|
Moisture content
|
%
|
<0.2
|
|
Width
|
mm
|
The mat`s width will be produced according to the customers` requirements.
|
3) S-BM (P) (Pull trussing type surface tissue)
The pull trussing type surfacing tissue could improve the strength of profiled material surface layer. It could ameliorate the capability and avoid crack of the product.
|
Item
|
Unit
|
Type
|
|
S-BM-90
|
S-BM-105
|
S-BM-120
|
|
Monofilament Diameter
|
µm
|
9 12
|
|
Area Weight
|
g/m2
|
90
|
105
|
120
|
|
Binder Content
|
%
|
<25
|
|
Penetrating time(two layers)
|
S
|
<25
|
<30
|
<40
|
|
Tensile Strength MD
|
N/50mm
|
>=280
|
>=300
|
>=350
|
|
Tensile Strength CD
|
N/50mm
|
>=180
|
>=200
|
>=230
|
|
Moisture content
|
%
|
<0.2
|
|
Width
|
mm
|
The mat`s width will be produced according to the customers` requirements.
|
|