CB-DWT is manufactured by co-extrusion of irradiated crosslinking polyolefin and specifically designed hot melt adhesive. This tubing may be used in a wide variety of electrical applications, including back end connector sealing, breakouts, and connector-to-cable transitions. High expansion ratio makes it possible to repair most damaged cable jackets without removing connectors.

Specifacations:
Material: Polyolefin
Products type: Dual-Wall with adhesive
Shrink ratio: 2: 1&3: 1&4: 1
Shrink Temperature: 110
Operating Temperature Range: -55'C -125'C
Tensile Strength (MPa): ≥10.4
Ultimate Elongation(%): ≥200
Radial shrinking ratio(%): ≥50
Longitudinal Change(%): ≤10
Aging in Circulating-air Oven: 158.0+/-1.0'C, 168hrs
Dielectric Strength(kV/mm ) ≥15.0
Flammability VW-1
Water Absorption(%) less than 0.4%
Fluid Resistance  Good to Excellent
(Copper Corrosion) No corrosion
Softening Point('C) 120+/-5
Tissue Strength(N/25mm): >80