Model: | Cemedine sx1008 |
---|---|
Brand: | CEMEDINE |
Origin: | Made In Japan |
Category: | Chemicals / Adhesives & Sealants |
Label: | SX1008 , SX1010 , RH96L |
Price: |
US $50
/ pc
|
Min. Order: | 10 pc |
Elastic adhesive | Thermal Conductive Elastic Adhesive SX-TCA series
Features
No concern for pump out (compared to grease)
Product data
Adhesive properties for various types of adherends
(Tensile shear strength :MPa)
Adherends | SX1008 | SX1010 | RH96L | |||
---|---|---|---|---|---|---|
Adhesive strength | Failure Modes | Adhesive strength | Failure Modes | Adhesive strength | Failure Modes | |
Hard polyvinyl chloride | 2.18 | CF | 1.61 | CF | 0.68 | CF1AF9 |
Polycarbonate | 2.16 | CF | 0.77 | AF | 0.82 | CF2AF8 |
Polystyrene | 1.98 | CF | 1.24 | AF | 0.61 | AF |
ABS | 2.10 | CF | 1.24 | CF5AF5 | 0.61 | AF |
Acryl | 2.20 | CF | 1.60 | CF | 0.28 | AF |
Nylon 6 | 1.66 | CF | 1.28 | CF | 0.65 | CF1AF9 |
Steel plate | 2.23 | CF | 1.50 | CF | 0.55 | AF7,Uncured3 |
Aluminum | 2.85 | CF | 1.90 | CF | 0.76 | AF |
* CF:Cohesion Failure, AF:Adhesive Failure
The numbers indicate their proportion to the adhesion area.
Surface treatment: Steel plate is MEK degreased, Plastic is IPA degreased
Coating quantity: Coated on both sides 100μm thick (per side)
Open time: SX1008, SX1010 No open-time, RH96L 2 minutes
Curing: 23°C 50%RH x 7 days
Tension speed: 50mm/min
Heat aging resistance(SX1008/SX1010)
(MPa)
SX1008 | SX1010 | |||||||
---|---|---|---|---|---|---|---|---|
120°C | 130°C | 120°C | 130°C | |||||
Initial value | 2.85 | CF | 2.85 | CF | 1.90 | CF | 1.90 | CF |
1W | 4.69 | CF | 4.82 | CF | 3.67 | CF | 3.88 | CF |
2W | 4.60 | CF | 4.10 | CF | 4.04 | CF | 3.81 | CF |
4W | 4.53 | CF | 3.98 | CF | 3.84 | CF | 3.70 | CF |
8W | 4.16 | CF | 3.01 | CF | 3.72 | CF | 3.20 | CF |
12W | 4.12 | CF | 2.48 | CF | 3.68 | CF | 2.96 | CF |
18W | 2.89 | CF | 1.99 | CF | 2.84 | CF | 2.54 | CF |
* CF:Cohesion Failure
Adherends: Aluminum (alumite)
Test method : JIS K6833
Heat aging resistance(RH96L)
(MPa)
150°C | ||
---|---|---|
Adhesive strength | Failure Modes | |
Initial value | 0.76 | AF |
100h | 0.89 | CF |
300h | 1.00 | CF |
500h | 1.19 | CF |
1000h | 1.52 | CF |
2000h | 2.22 | CF |
3000h | 2.58 | CF |
* CF:Cohesion Failure, AF:Adhesive Failure
Adherends: Aluminum (alumite)
Test method : JIS K6833
High-temperature and high-humidity test
(MPa)
85°C x 85%RH | SX1010 | |
---|---|---|
Adhesive strength | Failure Modes | |
Initial value | 1.90 | CF |
1W | 3.14 | CF |
2W | 3.23 | CF |
4W | 3.16 | CF |
8W | 3.43 | CF |
12W | 3.51 | CF |
18W | 3.67 | CF |
* CF:Cohesion Failure
Adherends: Aluminum (alumite)
Test method : JIS K6833
Thermal shock test
(MPa)
RH96L | ||||
---|---|---|---|---|
Adhesive strength | Failure Modes | Thermal conductivity | ||
Initial value | 0.76 | AF | 2.14 W/m・K | |
-40°C
↑↓ 125°C |
100 cycles | 1.28 | CF1AF9 | 2.04 W/m・K |
300 cycles | 1.46 | CF1AF9 | 2.15 W/m・K | |
500 cycles | 1.75 | AF | 2.06 W/m・K | |
1000 cycles | 2.04 | CF5AF5 | 2.71 W/m・K | |
2000 cycles | 2.59 | CF7AF3 | 2.82 W/m・K | |
3000 cycles | 3.02 | CF9AF1 | 2.81 W/m・K |
* CF:Cohesion Failure, AF:Adhesive Failure
The numbers indicate their proportion to the adhesion area.
Adherends: Aluminum (alumite)
Test method : JIS K6833
Property
Thermal Conductive Elastic Adhesive | |||||
---|---|---|---|---|---|
SX1008 | SX1010 | RH96L | |||
Application / Properties / Features | RoHS compliant
UL94 V-0 Equivalent |
||||
Low viscosity | High viscosity | Heat resistance | |||
Type | One-Component Type Elastic Adhesive | ||||
Base | Special acrylic-modified polymer | ||||
Appearance | White paste | White paste | Gray paste | ||
Viscosity | Pa・s/23°C | 120 | 650 | 250 | |
SVI | 2.0 | 4.2 | 4.5 | ||
Density | g/cm3 | 1.98 | 2.00 | 2.15 | |
Skin over time | 23°C | 3min | 3min | 7min | |
Cured properties | Hardness | Shore A | 84 | 85 | 65 |
Glass transfer point | °C | -62 | -62 | -44 | |
Breaking strength | MPa | 2.5 | 1.8 | 1.1 | |
Elongation at break | % | 30 | 20 | 45 | |
Thermal conductivity | W/m・K | 1.7 | 2.1 | 2.14 | |
Linear expansion coefficient | ppm/K | 77 | 55 | ||
Electric Characteristics | Volume resistivity | Ω・cm | 6.6 x 1012 | 1.3 x 1013 | 4.1 x 1011 |
Dielectric constant | 1MHz | 0.64 | 3.1 | 7.7 | |
Dielectric loss tangent | 1MHz | 0.01 | 0.12 | 0.46 | |
Insulation breakdown voltage | kV/mm | 38 | 22 | ||
Capacity | 135ml | 333ml
*Made to order |
333ml
*Made to order |
||
333ml |
Viscosity: BS-type rotational viscometer (Rotor No. 7, 10 rpm)
SVI: Viscosity ratio between 10 rpm and 1 rpm
Density: Based on the specific gravity cup method in JIS K6833
Thermal conductivity: Compliant with JIS A1412
Volume resistivity: Compliant with JIS K6911 (measurement voltage: 500 V)
Dielectric constant: Compliant with JIS K6911 5.14
Dielectric loss tangent: Compliant with JIS K6911 5.14
Insulation breakdown strength: Increase the voltage until insulation breakdown occurs, and measure the voltage limit
Price Terms: | FOB HONGKONG, FOB SHENZHEN |
---|---|
Payment Terms: | TT |
FU KAM INTL HONGKONG CO.,LTD | |
---|---|
Country/Region: | Guang Dong - China |
Business Nature: | Trading Company |
Phone: | 13590225219 |
Contact: | Billy.Lai (Sales Manager) |
Last Online: | 16 May, 2024 |