Gloria-Steel supplies as specialist of SA387Gr11C12,produces according to standard WYJ012-2001&ASME SA387,intended particularly for manufacturing of various structural parts working at atmosperic enviroment and corrosive gas or liquid.

Other grade:2 1/4Cr-1Mo,2.25Cr1Mo,15CrMo,13CrMo44,A387Gr22CL2,10CrMo9-10,12Cr2Mo1R,SA387Gr22CL2（9/4Cr-1Mo）,2.25Cr-1Mo-0.25V

Specifications following:

1.Thickness*width*length:8-200mm*1500-3900mm*3000-18000mm
2.Adopting standards: WYJ012-2001&ASME SA387
3.Dimensin,shape,weight and allowable deviation according to         standards:  GB6654-1996 or A20M
4.Supplied in the as-rolled condition:   Normalized+Tempered+S3+S5+S7 or Annealing or high-temperature   temper or Q&T
5.Chemical composition:
  C≤0.17,P≤0.010,S≤0.012,Mo 0.45-0.65
6.Mechanical property:
  Yield strength≥310MPa,Yield strength≥516-690MPa,Elongation   rate≥22%,Impact value at 10℃AKV≥54J(+10℃),425℃ yield   strength at MPa≥220;T≤25mm，d＝2a；25mm＜T≤50mm，d＝2.5a
  38mm---450℃S7，Rp0.2≥218.87Mpa；
  67mm---340℃ High-temperature tensile test,Rp0.2≥239.2Mpa；
  73mm---300℃ High-temperature tensile test,Rp0.2≥245.7Mpa；
7.Ultrasonic test: ASTM435/A435M-90  or S12(ASTM A578M-96)
8.Delivery time:30-60 days
9.Payment term:T/T or L/C
10.Minimal order: 1 pcs

More technology details and the MTC sample please visit our web site:www.gloriasteel.com or contact us.