Technical Data Sheet

 

 

NAR^® NT2000G

White Glossy Calendered PVC Vinyl

 

Features:

l  Soft and seamless vinyl, specially for solvent printers

l  Good sheet stability and lay flatness

l  Excellent printability, conversion and application characteristics

l  High gloss for superior appearance

l  High cost performance for short term promotional graphics

l  Excellent adhesion to a wide variety of substrates

 

 

Description

Film:                    100 micron glossy white, soft monomeric calendered PVC film

Adhesive:           Permanent clear solvent acrylic adhesive

Backing:             One side PE and silicon coated wood pulp paper, 140gsm

Width:         0.914/1.06/1.27/1.37/1.52m

Length:        50/100/250m

Shelf Life:      Up to 1 year at 20℃ and relative humidity of 50%

Durability:       Up to 1 year

 

 

Suit for:                                              Common Applications

Solvent inkjet   Eco solvent inkjet                    • Vehicle graphics

Cutting             Cold over laminating                             • Glass wall advertising

UV curable      Water based inkjet                             • Curve advertising

Screen printing Die Sublimation                      • Durable Signs and Labels

                                                                  • Exhibition graphics

 

 

 

Physical Characters

Properties	units	Test method	Average value
Thickness - film	µm	GB/T6672-2001	100±5
Weight- finished product Gloss 60° Initial Adhesion 180°Peel strength(steel,24h)	g/m² % N/inch N/inch	GB4669-1995 GB8807-88 FINAT9 FINAT1	290±20 70min 6min 11min
Dimensional stability MD	%	FINAT14	0.8max
Dimensional stability CD	%	FINAT14	0.5max
Elongation at break MD	%	GB/T1040.1-2006	140~260
Elongation at break CD	%	GB/T1040.1-2006	120~280
Tensile Strength at break MD	N/25 mm	GB/T1040.1-2006	50~90
Tensile Strength at Break CD Minimum application temperature Temperature range	N/25 mm °C °C	GB/T1040.1-2006	40~85 + 10 -20 ~ +70

ü   Information on physical characteristics is based upon tests we believe to be reliable. The values listed herein are average, minimum or maximum values. They are intended only as a source of information and are given without guarantee and do not constitute a warranty. Purchasers should independently determine, prior to use, the suitability of any material for their specific use.

ü   All technical data is subject to change without prior notice.

ü   In order to avoid loss of quality, the NAR product should be stored in suitable conditions, at temperature around 20℃ and relative humidity of 50%. Under this condition, NAR product can be stored for period of 1 year. When printing on

NAR media, the temperature setting is very important, and we s est an optimum printing condition of 25°C, 50%.

 

Test Method:

ü   Gross Degree:

Use a triangle gloss tester ,setting 60°，given testing data is surface gloss of products.

ü   Initial adhesion:

According to testing method (FTM-9,FINAT),remove release liner ,adhesive surface up ,make the specimen annular, to test peeling strength after a quick, complete touch between the specimen and glass.

ü   180°Peel strength(steel,24h):

(FTM-1, FINAT) is measured by peeling a specimen at a 180° angle from a stainless steel or float glass panel, 24 hours after the specimen has been applied under standardized conditions. Initial adhesion is measured 20 minutes after application of the specimen.

ü   Dimensional stability:

(FTM-14, FINAT)Is measured on a 150 x 150 mm aluminum panel to which a specimen has been