Addition cure silicone rubber Encapsulation and Poting compounds

Addition cure silicone rubber Encapsulation and Poting compounds
Model:LH-5035A
Brand:Lianhuan silicone
Origin:Made In China
Category:Electronics & Electricity / Insulation Material
Label:Addition cure rubber , poting silicone rubb , Encapsulationsilicon
Price: US $12.5 / kg
Min. Order:5 kg

Product Description

 

liquid silicone rubber of condensation type are multicomponent type which are named the RTV(Room Temperature Vulcanizing) as either one can be cured at room temperature. At the time of exposure in the air, gum elastic can be made progressing by crosslinking reaction with moisture.
Depending upon crosslinking type, silicone,s type could be divided into and residual things come

 I.Simple Use

Work can be done simply At room temperature, it cures to form rubber state with the humidity in the air without heating or any other special condition.

 II.Heatproof/Coldproof

After complete hardening, the adhesion and rubber elasticity can be kept for all continuous exposure in the range of -50oC~200oC.

III.Excellent Electric Characteris

In chemical structure, it shows excellent insulation. It keeps stable electricity even in the change of temperature, humidity, or environment, suitable for insulation or sealing for various electric and

IV.Chemical stability

Silicone sealant show excellent chemical resistance and oil resistance in comparesion with general organic rubber. When it contacts with certain engine oil, it may swell a little but, it is not decomposed not dissolved, it returns initial state when solvent is removed.

 V.Excellent Weatherproof

It shows excellent ultraviolet resistance. ozone resistance,and water resistance, which allows to keep original properties semi-permanently at outside use.

VI.Typical Product Data Properties

Items

Technique Request

Color

3018 White

3020 Black

2018 Clear

3525 Black

3020 White

Viscosity25,mpa.s

3000±500

3000±500

2000±200

3500±500

3000±500

Density(25.g/cm)

0.99±1.01

1.10±1.01

0.99±0.0.

1.10±0.02

1.10±0.02

Mixed Ratio()

5

5

5

5

A100:B10:C1

Viscosity After (25.g/cm)

2000±500

2000±500

1500±100

2500±500

2500±500

Work time(25min)

120180

120180

120180

120180

60120

Pot life(25,h)

78

78

78

78

45

Demoud time(25h)

24

24

24

24

24

Shore A Hardness (24h)

18±2

20±2

18±2

25±3

20±3

Shrinkage()

0.3

0.4

0.25

0.3

0.3

Use Temperature()

-60210

-60220

-60200

-60220

-60220

 

Volume resistivityΩcm

2.0×10

1.8×10

1.0×10

1.0×10

1.0×10

Dielectric Strength (kv.mm)

≥25

≥25

≥25

≥25

≥25

Permittivity (100kh)

2.9

2.9

2.9

3.0

3.0

Arc resistance (s)

80

80

80

80

80

Tensile(kn/m)

1.00

1.50

0.5

1.00

1.00

Tear strength(mpa)

0.80

1.50

0.5

1.00

1.00

Thermal conductivity W/(M.K)

0.15

0.15

0.15

0.15

0.15

thermal expansion (M/M)

1×10

1×10

1×10

1×10

1×10

Flame retardant

94-V0

94-V0

94-V0

* Testing is performed in accordance with current Lianhuan silicon material test methods, laboratory
* Typical property data values should not be use as specifications

VII.Packing
Silicone A Part : 1KG/Bottle, 25KG Pail
Hardner B Part: 1KG Bottle, 1.25KG Bottle

VIII.Keeping methods

Please keep components in shady and cold place, preventing from direct shining of sun and damp.

for any details information please contact shgslsl at 21cn dot com,


~Nancy xie
 lianhuan group limited

Phone:0086 13699849627
 Skype:nancyxie2007 

Http://www.lhsilicone.com

 

 

 

 

Addition cure silicone rubber Encapsulation and Poting compounds  1Addition cure silicone rubber Encapsulation and Poting compounds  2Addition cure silicone rubber Encapsulation and Poting compounds  3Addition cure silicone rubber Encapsulation and Poting compounds  4Addition cure silicone rubber Encapsulation and Poting compounds  5

Member Information

Shenzhen Lianhuan silicone Materail Co.,Ltd
Country/Region:Guang Dong - China
Business Nature:Manufacturer
Phone:13699849627
Contact:Betty Xu (Sales)
Last Online:02 Aug, 2017