Epoxy Resin AdhesiveTwo Component Epoxy Adhesives

Features

1. Reactive adhesive
2. Solventless
3. No gas produced during curing process
4. Excellent adhesive strength
5. Excellent heat and chemical resistance
6. Small shrinkage by curing
7. Small creep under load
8. Excellent durability
9. Superb insulation

   Application

   Applicable to Adherendss over an extensive range including metals and plastics

10. Adhesion of cars, vehicles, vessels and aircraft
11. Adhesion and sealing of electric equipment and electronic parts
12. Adhesion of composite members used for construction work
13. Assembly of precision equipment and artworks
14. Adhesion of sporting equipment

15. Product data

    Adhesive strength for various types of materials

    (Tensile shear adhesive strength: MPa)

    Adherends	1500	EP007	EP330
    Steel plate	15.5	14.8	7.8
    Aluminum	6.0	13.0	10.2
    Stainless steel	-	22.0	16.3
    Copper	7.8	10.0	19.8
    Hard polyvinyl chloride	3.5	4.1*	-
    Polystyrene	1.9	1.9	0.9
    Acryl	2.9	1.0	0.9
    FRP	12.3	8.0	3.9
    Melamine decorative board	5.4	-	43.1
    Lawan plywood	10.4*	10.0*	47.1*

    Chemical resistance test

    (Tensile shear adhesive strength: MPa)

    Chemicals	1500	EP007
    Initial value	15.5	14.8
    Aceton	12.5	17.6
    Toluene	12.5	17.3
    Trichloroethylene	12.8	17.4
    Methanol	12.0	17.4
    Gasoline	13.6	19.4
    Engine oil	11.2	21.5
    10% sulfuric acid	10.5	19.3
    10% NaOH	13.6	20.4
    Tap water	13.1	21.5

    Property

    Standard type

    			1500		Super
    			Base resin	Hardener	Base resin	Hardener
    Application / Properties / Features			General purpose use
    Type			Two-part epoxy adhesive curing at room temperature
    Base			Epoxy resin	Polyamide	Epoxy resin	Polyamide
    Appearance			Light yellow transparent	Light brown transparent	Light yellow translucent	Light brown transparent
    Viscosity		Pa･s/23°C	20	55	100	50
    Density		g/cm3	1.16	0.97	1.14	0.99
    Mixing ratio			1 : 1		1 : 1
    Standard curing conditions			23°C×24hours		23°C×24hours
    Pot life			Within 1 hour		Within 1 hour
    Time required for effective curing			6hours		6hours
    Adhesive property	Tensile shear strength	MPa	15.7		15.1
    	T-peel strength	N/mm	0.4
    Curing properties	Hardness	Shore D	82
    	Glass transfer point	°C	54
    	Coefficient of water absorption	%	0.8
    	Coefficient of linear expansion		7.1×10-5
    Electric Characteristics	Volume resistivity	Ω･cm	7.1×1015
    Capacity			500g	500g	15g set
    			1kg	1kg	40g set
    			3kg	3kg	110gset
    			15kg	15kg

    Fast curing type

    			High-super 5		High-quick		EP330/High-super 30		EP331
    			Base resin	Hardener	Base resin	Hardener	Base resin	Hardener	Base resin	Hardener
    Application / Properties / Features			5 minute epoxy		5 minute epoxy (antisagging type)		30 minute epoxy		30 minute epoxy (low-viscosity)
    Type			Two-part epoxy adhesive curing at room temperature
    Base			Epoxy resin	Polyamide	Epoxy resin	Polyamide	Epoxy resin	Polyamide	Epoxy resin	Polyamide
    Appearance			Blue translucent	Light yellow translucent	White	Gray	Pink translucent	Light yellow translucent	Light yellow translucent	Light yellow translucent
    Viscosity		Pa･s/23°C	125	65	600	400	70	160	4	7
    Density		g/cm3	1.17	1.15	1.57	1.50	1.17	1.14	1.16	1.16
    Mixing ratio			1 : 1		1 : 1		1 : 1		1 : 1
    Standard curing conditions			23°C×24hours		23°C×24hours		23°C×24hours		23°C×24hours
    Pot life			Within 5 minutes		Within 5 minutes		Within 30 minutes		Within 30 minutes
    Time required for effective curing			About 1 hour		About 1 hour		About 1 hour		About 1 hour
    Adhesive property	Tensile shear strength	MPa	18.0		17.7		17.5		17.6
    	T-peel strength	N/mm	0.31		0.40		0.47
    Curing properties	Hardness	Shore D	77				82		71
    	Glass transfer point	°C	47				43		41
    	Coefficientof water absorption	%	2.5				2.3		0.8
    	Coefficient of linear expansion		10.7×10-5				6.7×10-5		7.1×10-5
    Electric Characteristics	Volume resistivity	Ω･cm	4.9×1013				3.8×1011		2.4×1015
    Capacity			6g set		50g set		6g set		1kg	1kg
    			15g set		500g set		15g set
    			25g set				80g set
    			80g set				320mL set
    							3kg	3kg

    Transparent type

    			1565		1565+Hardener D		Excel-EPO
    			Base resin	Hardener	1565 Base resin	Hardener D	Base resin	Hardener
    Application / Properties / Features			30 minute epoxy (transparent)		High Transparent		10 minute epoxy (transparent)
    Type			Two-part epoxy adhesive curing at room temperature		Two-part thermosetting epoxy resin		Two-part epoxy adhesive curing at room temperature
    Base			Epoxy resin	Polythiol	Epoxy resin	Polyamide	Epoxy resin	Polythiol
    Appearance			Light yellow transparent	Red browntransparent	Light yellow transparent	Light yellow transparent	Colorless transparent	Colorless transparent
    Viscosity		Pa･s/23°C	1.5	1.5	1.5	0.001	20	20
    Density		g/cm3	1.15	1.24	1.15	0.83	1.14	1.13
    Mixing ratio			1 : 1		100 : 15		1 : 1
    Pot life		23°C	30 min		Within 3 hours		Within 10 min
    Time required for effective curing		23°C	9 hours		Heat curing		1 hour
    Standard curing conditions					60°C×2 hours
    Cured properties	Hardness	Shore D	72				78
    	Glass transfer point	°C					46
    	Coefficient of water absorption	%					2.3
    	Refractive index				1.55
    	Coefficient of linear expansion	ppm/K					8.3×10-5
    Electric Characteristics	Volume resistivity	Ω･cm					6.2×1013
    Capacity			500g	500g	500g	500g	15g set
    			1kg	1kg	1kg	1kg

    Flexible type

    			EP007		EP008
    			Base resin	Hardener	Base resin	Hardener
    Application / Properties / Features			Flexible type		Flexible type (antisagging)
    Type			Two-part epoxy adhesive curing at room temperature
    Base			Epoxy resin	Modified polyamide resin	Epoxy resin	Modified polyamide resin
    Appearance			Light yellow transparent	Light brown transparent	White translucent	Light brown transparent
    Non volatiles		wt%	99.7	99.0	99.0	99.0
    Viscosity		Pa･s/23°C	12	34	275	100
    Density		g/cm3	1.17	0.95	1.17	0.97
    Standard curing conditions			23°C×7 days		23°C×7 days
    			80°C×1 hour		80°C×1 hour
    Mixing ratio			1 : 1		1 : 1
    Pot life		23°C	60 min.		60 min.
    Time required for effective curing		23°C	12 hours		12 hours
    Tensile shear strength		MPa	22.0		23.0
    T-peel strength		N/mm	2.2		1.8
    Cured properties	Hardness	Shore D	78		74
    	Glass transfer point	°C	56		50
    	Elastic modulus	MPa	129
    	Coefficient of water absorption	%	0.7		1.8
    	Coefficient of linear expansion		9.7×10-5		12×10-5
    Electric Characteristics	Volume resistivity	Ω･cm	4.0×1015		1.50×1015
    	Surface resistivity	Ω/sq	1.2×1016		2.95×1016
    	Dielectric constant	1kHz	3.28		5.31
    	Dielectric loss tangent	1kHz	1.32×10-2		7.96×10-2
    Capacity			500g	500g	320ml set
    			15kg	15kg	500g	500g
    					15kg	15kg