Instantaneous Adhesive (Industrial Use)3000RXF/RXL/DLL/DXH/RXF/RS/3000RP/

Model:	3000RX 3000RXF
Brand:	CEMEDINE3000DLL/3000DXH/3000RXF/3000RS/3000RP
Origin:	Made In Japan
Category:	Chemicals / Adhesives & Sealants
Label:	3000RX/3000RXH , 3000RXF/3000RXM , 3000RXL
Price:	¥20 / pc
Min. Order:	25 pc

Inquire Now

Product Description

3000 Series

Mainly composed of alkyl-alpha-cyanoactylate, instantaneous adhesive is polymerized and cured by a small amount of moisture sucked on the surface of the adherend in a very short time (in several seconds).

Features

Quick curing
The instantaneous adhesive features the highest curing speed of all adhesives; curing is achieved in several seconds at a normal temperature.
Excellent adhesion
The instantaneous adhesive adheres to a great variety of adherends, providing powerful adhesion comparable to that of epoxy adhesive.
Simple adhesion
It is a one-part adhesive which does not require the use of hardener or catalyst. Furthermore, adhesion is completed by one drop of coating and gentle fixation.
Solventless adhesive
The instantaneous adhesive exhibits little curing shrinkage. It does not involve contamination of the work site environment due to organic solvent, as in the case of a rubber adhesive.

Application

• Adhesion of rubber parts	• Adhesion of electric, electronic, precision and automotive parts
• Adhesion of arts and crafts, personal ornaments, jewelry, toys, fishing tackle and sports goods	• Prevention of screws and bolts from getting loose
• Repair of cracks on natural stone	• Adhesion of porous materials (jelly, wood working)

List of Cemedine 3000 Series

Relationship between curing speed and adhesives

Set time and adhesion RX series

(Set time second: tensile shear strength N/mm²)
Product name	3000RX		3000RXF		3000RXL		3000RXM		3000RXH
Adherend	3		10		100		300		1,000
Steel	3		10		100		300		1,000
Aluminum	5	13.0	5	13.0	5	13.0	5	14.0	15	14.0
Copper	3	11.0	3	11.0	5	11.0	5	11.0	15	12.0
Chromium plated steel	3	10.0	3	10.0	5	10.0	5	10.0	15	11.0
ABS	3	10.0	3	10.0	5	10.0	5	10.0	15	11.0
Acrylic resin	2	5.0*	2	5.0*	2	5.0*	3	5.0*	3	0.5*
Polystyrene	10	6.0*	10	6.0*	20	6.0*	25	6.0*	30	6.0*
Unplasticized	5	4.0*	5	4.0*	10	4.0*	10	4.0*	20	4.0*
Polyvinylchloride	3	5.0*	3	5.0*	3	5.0*	3	5.0*	5	5.0*
Bakelite	5	7.0*	5	7.0*	5	7.0*	10	7.0*	15	7.0*
Nylon	5	6.0*	5	6.0*	5	6.0*	10	6.0*	15	6.0*
Polycarbonate	5	10.0*	5	10.0*	5	10.0*	10	10.0*	15	10.0*
NR	1	0.5*	1	0.5*	1	0.5*	2	0.5*	3	0.5*
CR	1	0.5*	1	0.5*	1	0.5*	2	0.5*	3	0.5*
SBR	1	0.6*	1	0.6*	1	0.6*	1	0.6*	3	0.6*
NBR	1	2.7*	1	0.7*	1	0.7*	2	0.7*	3	0.7*
EPDM	1	1.1*	1	1.1*	1	1.1*	1	1.1*	3	1.1*
TPE	3	1.8*	3	1.8*	5	1.8*	5	1.5*	10	1.1

Asterisk (*) indicates material failure, and TPE indicates olefinic thermoplastic elastomer.
Viscosity (mPa・s/23°C)

Peeling strength for various materials DX series

(unit: N/mm)
Viscosity	3000DXL (Middle viscosity type)	3000DXH (high viscosity type)	Ethyl standard
Adherend	3000DXL (Middle viscosity type)	3000DXH (high viscosity type)	Ethyl standard
Steel plate (grinding)	1.96	3.12	0.32
Steel plate	1.16	2.76	0.2
Aluminum	3.12	3.12	0.2
Stainless steel	1.16	3.52	0.2
Copper	0.8	1.56	0.08
Zinc	1.56	1.96	-

Test conditions

T-formed peeling strength is 50mm/min. in conformity to JIS K6854.
After being degreased with acetone and toluene at the mixing ratio of 1 to 1, each test piece is cured at the normal temperature for 48 hours; then it is measured.

Set time and adhesion for steel RX series

Adhesion for adhesion-resistant materials RX series

Adhesive durability DX series

High strength and durability DX series

Polyolefin adhesion system Cemedine PPX+ PPX-3 (cyanoacrylate adhesive) (primer)

Adhesion of adhesion-resistant materials such as polyethylene, polypropylene, polyacetal, and silicon rubber in a short time. (Combined use of surface modification primer PPX-3 and cyanoacrylate adhesive Cemedine PPX)