Product Name: Zinc
Click to view: Hebei Metallurgical Research Institute Testing Center Results
Click to view: Zinc Production
Product Name: Zinc powder
Formula: Zn
Weight: 65.38
Physical properties: light gray metallic fine powder
Chemical properties: Insoluble in water, soluble in acid and alkali, slowly soluble in acetic acid, ammonia.With a strong reduction, and acid-base hydrogen. Wet agglomeration, stable in dry air, moist airgenerated basic carbonate white and overlying the surface. Air blue green flame combustion to generate zinc oxide. And high purity sulfuric acid, nitric acid slowly, when a small amount of other metalssuch as steel, tin, lead when the reaction speed.
Technical Specifications
Item / Specification
|
Chemical Composition |
Particle Size |
||||||
Whole Zinc(%) |
Metallic Zinc(%) |
Lead
|
Ferrum (%) |
Cadmium(%) |
Mean Particle Size μm |
Maximum Particle Sizeμm |
Screenings(%) |
|
2000mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
≤2 |
≤6.5 |
≤0.1 |
1500mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
≤3 |
≤8 |
≤0.1 |
800mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
≤5 |
≤15 |
≤0.1 |
600mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
≤6 |
≤22 |
≤0.1 |
500mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
≤7 |
≤25 |
≤0.1 |
400mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
≤8 |
≤38 |
≤0.1 |
325mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
≤9 |
≤45 |
≤0.1 |
200mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
|
|
≤0.1 |
120mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
|
|
≤0.1 |
80mesh |
≥98 |
≥96 |
≤0.1 |
≤0.05 |
≤0.1 |
|
|
≤0.1 |
Product Features: Our highly-active zinc powder features high content of metallic zinc, low content of other impurity elements, smooth particle surface, big specific surface area, low apparent density, little surface oxidation, seldom fusion, transformation and grape-shaped particle adhesion. The total content of zinc is above 99% and the content of metallic zinc is above 97%.
Grade |
Chemical Composition |
|||||
Whole Zinc(%) |
Metallic Zinc(%) |
Lead(%) |
Ferrum(%) |
Cadmium(%) |
Matters Insoluble in Acid(%) |
|
Grade Ⅰ |
≥99.5 |
≥98.0 |
≤0.005 |
≤0.003 |
≤0.008 |
≤0.05 |
Grade Ⅱ |
≥99.3 |
≥97.5 |
≤0.01 |
≤0.003 |
≤0.009 |
≤0.07 |
Grade Ⅲ |
≥99.0 |
≥97.0 |
≤0.01 |
≤0.003 |
≤0.01 |
|
Product Use
Chemical production:
For insurance powder (Ci sodium), lithopone (lithopone), carved white block (sodium bisulfate formaldehyde), dye intermediates such as the production of a larger amount of reducing agent, particle size slightly compared with zinc coating rough average particle size of 10-12μm.
Zinc corrosion coating production:
Steel components zinc metal corrosion is the main purpose, there are hot dip coating method, plating, thermal spraying, zinc-rich paint, powder coating, etc., which is the most important method of Redu.Mainly used for hot-dip zinc-rich coating and electroplating unsuitable large components, such as a large outdoor steel (marine engineering, bridges, pipelines, highway guardrail, etc.), ships, containers and other coating. According to different film base material, zinc-rich coating can be divided into organic and inorganic zinc-rich coating zinc-rich coating. Organic zinc-rich coatings used epoxy ester, epoxy resin, chlorinated rubber, ethylene-based resin and polyurethane resin as the film base material, the content of zinc in the dry film in the 85% -92%. Inorganic zinc-rich paint with water-based lithium silicate, potassium silicate, water, mud or water TEOS as the base material, zinc content in the dry film 92%. Zinc coating, the average particle size of 2-3μm and 5-7μm two specifications, the powder was a narrow grain size distribution, good dispersion.
Mechanical plating and galvanizing production infiltration:
Mainly used for screws, nails, wire, nail and other mechanical galvanizing, my company for the production and use of mechanical galvanizing process to produce refined zinc, airflow speed multi-level granularity from 300-1500 purpose combination agencies, major Specifications 5 #, 6 #, 8 #, 10 #, suitable for different levels of technical standards required mechanical galvanizing process, coating smooth. In addition, I produced for diffusion coating technology requires a special zinc, with a particle size distribution, in the course of easy oxidation characteristics.
Hydrometallurgy:
Replacement for solution purification and metal recycling, such as refining gold, silver, non-ferrous metals
Pharmaceuticals and pesticides:
Zinc as a reducing agent for the production of salicylic acid, indomethacin, aminopyrine, etc., as a raw material for the production of Zineb, zinc phosphide, efficiency and low toxicity pesticides daisy enzymes.
Other
Packing: steel drums and woven bag lined with plastic barrel (bags) net weight 50KG, or according to customer requirements.
Transport and storage:
1, zinc during transport should be moisture, fire, impact and avoid falling.
2, zinc powder should be stored in ventilated, dry and fireproof warehouse.
Jiangsu branch into non-ferrous metal new material co., LTD | |
---|---|
Country/Region: | Jiang Su - China |
Business Nature: | Manufacturer |
Phone: | 13270790992 |
Contact: | zhen liu (Please provide your ) |
Last Online: | 15 Dec, 2014 |