1. Constitution Structure:
Top Coating PVDF/Nano-PVDF (KYNAR 500)
Aluminum skin
Macromolecular lamination film
Nontoxic polyethylene core or No-combustible filled core
Macromolecular lamination film
Aluminum skin
Service coating or mill finished
2. Characteristic:
Fire safety: The outer aluminum sheets and the inner fire-resist polyethylene function the panel having an excellent fireproof performance, and meeting the standard_smoke less and no harmful gas.
Weather-resistance: Superior weather-resistance and ultraviolet (UV) resistance, acid-resistance and alkali-resistance, suitable for all natural environments.
Smooth Surface: The fire-resist ACP provide superior and smooth surface, coated with the PVDF inheriting the excellent surface characteristics, satisfying the modern building with perfect appearance.
High Strength: The fire-resist ACP use high quality aluminum with the high quality fire-resist polyethylene core which can be greatly enhanced strength, ensure the performance of wind-pressure resistance, shockproof, and anti-impact.
Easy Processing: ACP is easy to cut, slot, punch, bend into circular, rectangular and other shapes also can be designed to various modeling according to your ideas.
Exertion Design: The fire-resist ACP has series of glossy and shape to meet the designer great originality, achieve perfect results.
3. Specification
Thickness: 2mm, 3mm, 4mm, 5mm, 6mm
Alu thickenss: 0.06-0.50mm
Width: 900 ≤ W ≤ 1600
Length: Customized
| Application: |
Interior Decoration, Exterior Wall Cladding and Sign |
| Dimensional Tolerances |
Thickness(mm) |
±0.2 |
| Width(mm) |
±2 |
| Length(mm) |
±3 |
| Diagonal(mm) |
±5 |
| Thermal Expansion |
2.4mm/m at 100 ºC temp difference |
| Aluminum Thickness(mm) |
±0.02 |
| Surface Properties |
Pencil Hardness |
>HB/>2H |
| Temperature Resistance |
-50 ºC to +80 ºC |
| Impact strength (kg. cm) |
50 |
| Boiling Resistance |
Boiling for 2 hours without change |
| Acid Resistance |
Immerse Surface in 2% HC1 for 48 hours without change |
| Alkali Resistance |
Immerse Surface in 2% NAOH for 48 hours without change |
| Oil Resistance |
Immerse Surface in 20# engine oil for 48 hours without change |
| Solvent Resistance |
Cleaned 100 times with dimethylbezene without change |
| Cleaning Resistance |
Over 1000 times without change |
| Peel Strength 180 ºC |
180oC>5 newton/mm |
| Product Properties |
Sound Absorption NRC |
0.05 |
| Sound Attenuation RW db |
23/24/25 |
| Water Absorption % by volume |
0.0047/0.0057/0.0012 |
| Core Composition |
LDPE Polyethylene, Non- Combustible Material |