The workpiece easily gets damp after being immersed in fluxing tank, because the ammonium chloride in galvanizing agent solution contains water of crystallization. And long time of dryness or buying drying equipment can solve this problem. In real hot galvanizing production, the molten zinc may splash while putting the workpiece with galvanizing agent solution on it not completely dry into zinc pot, which may results in wastage of molten zinc and endangering personal safety of workers; the traditional hot dip galvanizing adopts drying technics, which may cause low production efficiency, besides, because of beyond drying, galvanization-missing may occur and influence quality of galvanized products. For example, in hot galvanizing of cast iron and steel workpiece, this problem usually exists.  

The appearance of detonation inhibitor solves the above problems, it is composed with high surface active agent and steel wetout agent, etc, which can make water spread on surface of workpiece, with no bead of water appears, and eliminate or reduce zinc explosion of workpiece. It can not only make up the shortage of preceding process, but also active surface of steel further, raise the quality of hot dip galvanizing. This is not included in other steel anti-corrosion technics. It can raise quality of galvanizing coating, reduce zinc consumption and production cost obviously by using the detonation inhibitor.