Silicone ink Appliation                                                 :

Suitable for most natural and synthetic fabrics, including elastic fabrics for these garments:

·                  Jerseys

·                  Hats & caps

·                  Sweaters

·                  Jackets

·                  Gloves

·                  Sleepwear

·                  Pants & shorts

·                  Bathing suits

·                  Undergarments

·                  Uniforms

·                  Shirts

·                  Sweatshirts

 

Silicone Ink features                                                  :

·                  Good hand feel: Soft, non-sticky handle with no blocking problem upon folding

·                  Excellent durability: Wash- and weather-resistance

·                  Color fastness: No color migration, even between red and white

·                  Improved fashion appearance: Semi-gloss finish with no creasing

·                  High elongation: Suitable for fabric with Lycra content

·                  Fast cure: Skin cures in 3 to 6 seconds at skin temperatures between 100-130°C

·                  Operation-friendly: Suitable viscosity and thixotropy for manual screen printing

·                  Easily pigmented: A base gel / catalyst system of less than 10 percent

·                  Environmentally sound: Does not contain organotin, phthalate, formaldehyde, PVC or solvent

·                  Reduced total cost of use: Lower process time and better coverage

·                  Low shrinkage(<0.1%)

·                  Excellent performance of anti-slip

·                  Good skid-proof effect and high adhesive strength

·                  Wearproof, wash-resistant, high temperature resistant

·                  Non-toxic and odorless, food grade silicone

·                  High transparency and good tear-strength

·                  Wearproof, washable, high temperature resistance

·                  Three-dimensional level

·                   

Silicone Ink Datasheet                                 :

 

Model	901040	903540
Appearance	Transparent	Transparent
Hardness(shore A)	35±2	42±2
Mix ratio(A:B)	10:1	10:1
Viscosity(mPa.s)	60000~100000	300000~380000
Tensile strength(Mpa)	4.6	4.8
Tear-strength(KN/m)	20±2	22±2
Elongation(%)	450	420
Pot life/working time(25degree)	2-3 hours	2-3 hours
curing time(125degree)	30~50 seconds	30~50 seconds

 (ps: the hardness and viscosity is adjustable)

 

Silicone Ink Prepare Methods                                  :
Mixed Color master batch: Using it when needing various colors.

For ink to be yellow: first change base A part to white color (10%) white pigment in. then mixed with yellow color paste1% to colors!
Same process as for ink to blue and Red ink!
 

For ink to be black :  add 5% of black color paste to base A part mixed well.
 

For ink to be grey:  add 3% of black color paste and 5% of white color paste to base A part mixed well

Silicone Ink Mix process                                          :

 

1.   Mixed 10% CATATLYST curing agent B Part into small amount of silicone ink A Part(90%).
2.   The curing agent should be mixed very well，Otherwise，some parts won’t be cured.
3.   could use thinner for decrease the viscosity，over 15% of thinner, the abrasiveness, durability and adhesion force will be reduce. There tested before production is required.

Silicone Ink Drying Methods                                      :

1. According to different thickness of silicone ink, the curing time is different. Normal situation for mixing Part A: Part B =10:1 curing time is 50seconds with the temperature of 150degree (polyaddition process).
2. When the room temperature is above 25degree (humidity 50%), room temperature cure can be carried out under summer condition
3.Color master batch: Using it when needing various colors.

 

Quality Inspection

 

More details, please contact MS Nancy Xie                           

Phone: 0086-13699849627                                           

Skype: nancyxie2007                                                

Website: www (dot) lhsilicone (dot) com