Thermoplastic Polyolefin(TPO) Waterproofing Membrane
| Model: | TPO-H |
|---|---|
| Brand: | STARRING |
| Origin: | Made In China |
| Category: | Construction & Decoration / Waterproof Materials |
| Label: | waterproof , tpo waterproof , waterproof material |
| Price: |
US $9.5
/ sqm
|
| Min. Order: | 1000 sqm |
Product Description
Thermoplastic Polyolefin(TPO) Waterproofing Membrane
Products Description
TPO waterproofing membrane combines both polypropylene (plastic) and ethylene-propylene (rubber) using
state-of-the-art polymer manufacturing technology.Plasticizer-free TPO membrane deliver long-term flexibility. The result is an ideal commercial waterproofing membrane that is reliable, cost effective,
environmentally friendly and easy to install.
Product Features
1.High UV-resistance and high reflectivity
2. Excellent weathering characteristics and long-term flexibility
3.High tensile strength and puncture resistance
4. Excellent resistance to harsh chemicals and industrial pollutants
5.Heat or solvent-welding effectively provides seamless roof coverings
Products Specification
Length:15m 20m 25m
Width:1m 2m
Thickness:0.5mm 1.0mm 1.2mm 1.5mm 1.8mm 2.0mm
Color:black,white,green etc.,or customized
Product Technical Parameters
|
No. |
Test Item |
Indicators |
||||||
|
H |
L |
P |
G |
GL |
||||
|
1 |
The thickness of resin layer above the reinforcement fabric mm≥ |
— |
0.40 |
|||||
|
2 |
Stretching Performance |
Maximum Tension N/cm ≥ |
— |
200 |
250 |
|
200 |
|
|
Tension Strength Mpa≥ |
12 |
|
|
12 |
|
|||
|
Max. Tension Elongation ≥ |
|
|
15 |
|
|
|||
|
Breaking Elongation≥ |
500 |
250 |
|
400 |
200 |
|||
|
3 |
Heating Treatment Size Change Rate≤ |
2.0 |
1.0 |
0.5 |
0.1 |
0.1 |
||
|
4 |
Low-temperature Bending |
-40°C -40°C No Craze |
||||||
|
5 |
Water Impermeability |
0.3Mpa,2h Water Impermeability |
||||||
|
6 |
Impact Resistance |
0.5kg·m , Water Impermeability |
||||||
|
7 |
Anti-static Loada |
—
|
20kg Water Impermeability |
|||||
|
8 |
Seam Peel Strength N/mm ≥ |
4.0or Membrane Breaking
|
3.0 |
|||||
|
9 |
Right-angle Tear Strength N/mm ≥ |
60 |
|
— |
60 |
— |
||
|
10 |
Trapezoid Tear Strength N≥ |
— |
300 |
450 |
— |
350 |
||
|
11 |
Water Absorbing Capacity (70°C168h) |
After Soaking ≤ |
4.0 |
|||||
|
After Airing≥ |
-0.40 |
|||||||
|
12 |
Heat aging(80°C) |
Time |
672h |
|||||
|
Appearance |
No blisters, cracks, delamination, bonding and holes |
|||||||
|
Tensile Strength (max. tensile)Retention≥ |
90 |
|||||||
|
Elongation Retention ≥ |
90 |
|||||||
|
Cold Bending |
-40°C No Craze |
|||||||
|
13 |
Chemical Resistance |
Appearance |
No blisters, cracks, delamination, bonding and holes |
|||||
|
Tensile Strength (max. tensile)Retention ≥ |
90 |
|||||||
|
Elongation Retention ≥ |
90 |
|||||||
|
Cold Bending |
-40°C No Craze |
|||||||
|
14 |
Artificial climate accelerating ageing |
Time |
1500hb |
|||||
|
Appearance |
No blisters, cracks, delamination, bonding and holes |
|||||||
|
Tensile Strength (max. tensile)Retention ≥ |
90 |
|||||||
|
Elongation Retention ≥ |
90 |
|||||||
|
Cold Bending |
-40°C No Craze |
|||||||
|
a Anti-static loading is only applied to the roofing membrane. bThe artificial climate accelerated time is 2500 hours for single roofing membrane. |
||||||||
Member Information
| Laiwu Starring Trading Co., Ltd | |
|---|---|
| Country/Region: | Shan Dong - China |
| Business Nature: | Trading Company |
| Phone: | 15154093589 |
| Contact: | Bella Wang (Foreign Trade Salesm) |
| Last Online: | 10 Jul, 2013 |