LD-007 epoxy grouting material including A (resin) and B (hardener), C (filler), The product uses high-quality resin and refined packing, 100% solids, solvent and other volatile harmfulsubstances. Room temperature, the three groups were completely mixed in each group of materials can be used, without having to add any additional ingredients. LD-007 epoxy grouting material to withstand vibration, shock and chemical corrosion region required a long period of secondary grouting equipment installation provides a permanent solution has been proven to greatly extend the operating cycle of the mobile device and component life.
(1) Uses:
And secondary grouting for compressors, pumps, punching machine, mill, ball mill, high vibration equipment installation.
Used for the the grouting equipment base area susceptible to chemical attack.
Used to track foundation, bridge support strong pressure region grouting.
For anchor, reinforced planting and structural concrete reinforcement.
Features:
Compressive strength, bonding and other physical and mechanical properties far superior to cement-based grouting material.
Reaction curing mild, low exothermic peak of up to 90 minutes (25 ° C), hours of operation, suitable for large volume filling.
No shrinkage: no shrinkage after grouting molding to ensure high accuracy required for installation.
Corrosion resistance: long-term contact corrosion with acid, alkali, salt, oil and other chemicals.
Excellent creep resistance: LD-007 -80 ° C to +80 ° C alternate freezing and thawing, the harsh physical conditions of long-term use without plastic deformation vibration pressure to ensure long-term precision positioning equipment.
Remarkable resilience: LD-007 can be resolved by the mobile device to any possible transfer of the cement-based grout layer burst dynamic load
3 Physical Performance target
Item Index value detection value test
Compressive strength (the final result MPa) 90-105 103 GB/T50081-2002
Flexural strength (the final result, MPa) 25-35 32 GB/T50081-2002
Modulus of elasticity (the final result, MPa) 17-20 18 GB/T50081-2002
Coefficient of thermal expansion (final result) <of 40 × 10-6mm/mm / ° C GBJ119-88
Linear shrinkage (final result) ----- HG/T2625-94