| Model: | H-168 |
|---|---|
| Brand: | H3O |
| Origin: | Made In China |
| Category: | Chemicals / Adhesives & Sealants |
| Label: | one component , polyurethane sealant , adhesive |
| Price: |
¥18
/ pc
|
| Min. Order: | 1000 pc |
| Last Online:26 Mar, 2019 |
Product feather:
(1) One component, good contact deformation, easy to construct
(2) High strength.
(3) Good compatibility and wide use.
(4) Environmental friendly, pass SGS, E tandard certification.
(5) High elasticity and good adhesion.
(6) Resistant to water, oil and aging.
(7) No solvent, no shrinkage after curing.
Using way
Suitable for bonding and sealing among various materials such as metal, alloy, glass, wood, concrete, marble and ceramics. Can be applied to the construction industry, industry, transportation industry, home appliance industry, furniture industry and other industries. To do some adhesion test before a large number of use. If necessary, do roughening or adding primer before adhesion.
Product standard: HG/T 4363-2012, GB/T 30512-2014
Technical characteristic:
|
Appearance |
Black paste（before curing）、 Black rubber（after curing） |
Peeling adhesion(white glass, lacquered steel plate) |
white glass |
100% cohesion failure |
|
lacquered steel plate |
100% cohesion failure |
|||
|
Density（before the curing） |
1.36g/cm3 |
Low temperature flexibility |
No cracks |
|
|
Sagging degree |
0mm |
100% constant tensile stress |
2.9MPa |
|
|
Shore hardness |
59.8 Shore A |
Tensile strength |
7.1MPa |
|
|
Surface drying time |
40min |
Elongation at break |
408% |
|
|
Curing speed |
3.3mm/24h |
Tear strength |
18MPa |
|
|
Non-volatile matter content |
99.5% |
Shear strength（4h，8h，168h） |
4h |
0.12MPa |
|
8h |
0.50MPa |
|||
|
168h |
3.58MPa |
|||
Packing specification:
310ml aluminum tube packing, 400ml flexible package, 600ml flexible package.
Storage and expiry date:
In 5-25℃，dry place storage life of 9 months.