Product feather
(1) One component, easier to use. Avoid the waste of used up after mixing on the construction site.
(2) Room temperature moisture curing. Without heating, construction temperature range wide, 5 to 40℃ under the condition of construction.
(3) High solid content, will not cause shrinkage and depression after use.
(4) Good weather resistance. Resistant to vibration fatigue, suitable for elastic seal.
(5) No harmful substances will be produced during and after curing, the product has passed the SGS and E est, and the product conforms to GB/T 30512-2014, with no pollution to the base material.
(6) The surface can be painted, the surface can be coated with a variety of paints and coating.
Using way
(1) Adhesive the automobile glass
(2) Sealing the automobile glass
(3) Suitable for flexible sealing and bonding
(4) Car fixing
Product standard: HG/T 4363-2012, GB/T 30512-2014
Technical characteristic:
|
Appearance |
Black paste（before curing）、 Black rubber（after curing） |
Peeling adhesion(white glass, lacquered steel plate) |
white glass |
100% cohesion failure |
|
lacquered steel plate |
100% cohesion failure |
|||
|
Density（before the curing） |
1.36g/cm3 |
Low temperature flexibility |
No cracks |
|
|
Sagging degree |
0mm |
100% constant tensile stress |
2.9MPa |
|
|
Shore hardness |
59.8 Shore A |
Tensile strength |
7.1MPa |
|
|
Surface drying time |
40min |
Elongation at break |
408% |
|
|
Curing speed |
3.3mm/24h |
Tear strength |
18MPa |
|
|
Non-volatile matter content |
99.5% |
Shear strength（4h，8h，168h） |
4h |
0.12MPa |
|
8h |
0.50MPa |
|||
|
168h |
3.58MPa |
|||