PC/ABS C6200 |
|
|
CYCOLOY ™ Resin C6200 |
SI |
| British |
| Metric |
|
Americas: COMMERCIAL |
|
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs. |
|
Property |
|
TYPICAL PROPERTIES (1) |
||||
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress, yld, Type I, 50 mm/min |
680 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain, brk, Type I, 50 mm/min |
50 |
% |
ASTM D 638 |
|
Flexural Stress, yld, 2.6 mm/min, 100 mm span |
1050 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus, 2.6 mm/min, 100 mm span |
27400 |
kgf/cm² |
ASTM D 790 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact, notched, 23°C |
54 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Energy @ peak, 23°C |
622 |
cm-kgf |
ASTM D 3763 |
|
Instrumented Impact Energy @ peak, -30 |
553 |
cm-kgf |
ASTM D 3763 |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT, 1.82 MPa, 3.2mm, unannealed |
87 |
°C |
ASTM D 648 |
|
HDT, 1.82 MPa, 6.4 mm, unannealed |
90 |
°C |
ASTM D 648 |
|
Relative Temp Index, Elec |
85 |
°C |
UL 746B |
|
Relative Temp Index, Mech w/impact |
85 |
°C |
UL 746B |
|
Relative Temp Index, Mech w/o impact |
85 |
°C |
UL 746B |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.18 |
- |
ASTM D 792 |
|
Mold Shrinkage, flow, 3.2 mm (5) |
0.4 - 0.6 |
% |
SABIC Method |
|
Mold Shrinkage, xflow, 3.2 mm (5) |
0.4 - 0.6 |
% |
SABIC Method |
|
Melt Flow Rate, 260°C/2.16 kgf |
14.5 |
g/10 min |
ASTM D 1238 |
|
Spiral Flow,260°C,10 ips,3.175 X 1524 mm |
685.8 |
mm |
- |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Arc Resistance, Tungsten {PLC} |
6 |
PLC Code |
ASTM D 495 |
|
Hot Wire Ignition {PLC) |
2 |
PLC Code |
UL 746A |
|
High Voltage Arc Track Rate {PLC} |
3 |
PLC Code |
UL 746A |
|
High Ampere Arc Ign, surface {PLC} |
0 |
PLC Code |
UL 746A |
|
Comparative Tracking Index (UL) {PLC} |
2 |
PLC Code |
UL 746A |
|
Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
|
Surface Resistivity, ROA |
>1.E+15 |
Ohm |
IEC 60093 |
|
Dielectric Strength, in oil, 0.8 mm |
35 |
kV/mm |
IEC 60243-1 |
|
Dielectric Strength, in oil, 1.6 mm |
25 |
kV/mm |
IEC 60243-1 |
|
Dielectric Strength, in oil, 3.2 mm |
17 |
kV/mm |
IEC 60243-1 |
|
Relative Permittivity, 1 MHz |
2.7 |
- |
IEC 60250 |
|
Dissipation Factor, 50/60 Hz |
0.004 |
- |
IEC 60250 |
|
Dissipation Factor, 1 MHz |
0.008 |
- |
IEC 60250 |
|
Relative Permittivity, 50/60 Hz |
2.8 |
- |
IEC 60250 |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Recognized, 94HB Flame Class Rating (3) |
0.71 |
mm |
UL 94 |
|
UL Recognized, 94V-1 Flame Class Rating (3) |
1.21 |
mm |
UL 94 |
|
UL Recognized, 94V-0 Flame Class Rating (3) |
1.47 |
mm |
UL 94 |
|
UL Recognized, 94-5VA Rating (3) |
3.4 |
mm |
UL 94 |
|
UL Recognized, 94-5VB Rating (3) |
2 |
mm |
UL 94 |
Source GMD, last updated:2000/01/05 |
Processing |
Parameter |
||
Injection Molding |
Value |
Unit |
Drying Temperature |
80 - 90 |
°C |
Drying Time |
3 - 4 |
hrs |
Drying Time (Cumulative) |
8 |
hrs |
Maximum Moisture Content |
0.04 |
% |
Melt Temperature |
245 - 275 |
°C |
Nozzle Temperature |
245 - 275 |
°C |
Front - Zone 3 Temperature |
245 - 275 |
°C |
Middle - Zone 2 Temperature |
220 - 275 |
°C |
Rear - Zone 1 Temperature |
220 - 255 |
°C |
Mold Temperature |
60 - 80 |
°C |
Back Pressure |
0.3 - 0.7 |
MPa |
Screw Speed |
40 - 70 |
rpm |
Shot to Cylinder Size |
30 - 80 |
% |
Vent Depth |
0.038 - 0.076 |
mm |
Source GMD, last updated:2000/01/05 |
• NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding. |
|
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. |
|
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(6) Needs hard coat to consistently pass 60 sec Vertical Burn.
Disclaimer : THE MATERIALS, PRODUCTS AND SERVICES OF SAUDI BASIC INDUSTRIES CORPORATION (SABIC) OR ITS SUBSIDIARIES OR AFFILIATES (“SELLER”) ARE SOLD SUBJECT TO SELLER’S STANDARD CONDITIONS OF SALE, WHICH ARE AVAILABLE UPON REQUEST. INFORMATION AND RECOMMENDATIONS CONTAINED IN THIS DOCUMENT ARE GIVEN IN GOOD FAITH. HOWEVER, SELLER MAKES NO EXPRESS OR IMPLIED REPRESENTATION, WARRANTY OR GUARANTEE (i) THAT ANY RESULTS DESCRIBED IN THIS DOCUMENT WILL BE OBTAINED UNDER END-USE CONDITIONS, OR (ii) AS TO THE EFFECTIVENESS OR SAFETY OF ANY DESIGN OR APPLICATION INCORPORATING SELLER’S MATERIALS, PRODUCTS, SERVICES OR RECOMMENDATIONS. UNLESS OTHERWISE PROVIDED IN SELLER’S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS, PRODUCTS, SERVICES OR RECOMMENDATIONS DESCRIBED IN THIS DOCUMENT. Each user is responsible for making its own determination as to the suitability of Seller’s materials, products, services or recommendations for the user’s particular use through appropriate end-use and other testing and analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller’s Standard Conditions of Sale or this Disclaimer, unless it is specifically agreed to in a writing signed by Seller. Statements by Seller concerning a possible use of any material, product, service or design do not, are not intended to, and should not be construed to grant any license under any patent or other intellectual property right of Seller or as a recommendation for the use of any material, product, service or design in a manner that infringes any patent or other intellectual property right.
SABIC and brands marked with ™ are trademarks of SABIC or its subsidiaries or affiliates.
© 2014 Saudi Basic Industries Corporation (SABIC). All Rights Reserved.