LCP 日本新石油化學 MG350注塑級
物性表 |
|||||
|
|||||
性能項目 |
測試條件 |
測試方法 |
數值/描述 |
單位 |
|
機械性能 |
拉伸強度(引張強度) |
|
ASTM D638/ISO 527 |
102 |
kg/cm²(MPa)[Lb/in2] |
拉伸模量 |
|
ASTM D638/ISO 527 |
|
kg/cm²(MPa)[Lb/in2] |
|
拉伸屈服伸長率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
|
拉伸斷裂伸長率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
|
彎曲模量(彎曲彈性率) |
|
ASTM D790/ISO 178 |
16 |
kg/cm²(MPa)[Lb/in2] |
|
彎曲強度 |
|
ASTM D790/ISO 178 |
140 |
kg/cm²(MPa)[Lb/in2] |
|
IZOD 缺口衝擊強度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
97 |
kg·cm/cm(J/M)ft·lb/in |
|
1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
Charpy衝擊強度 |
23℃ (缺口) |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
|
-30℃(缺口) |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
23℃(無缺口) |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
-30℃(無缺口) |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
物性性能 |
比重(密度) |
|
ASTM D792/ISO 1183 |
1.78 |
|
吸水率 23℃/24H |
|
ASTM D570/ISO 62 |
<0.1 |
% |
|
熱性能 |
熱變形溫度 |
退火 |
ASTM D648/ISO 75 |
256 |
℃(℉) |
未退火 |
ASTM D648/ISO 75 |
|
℃(℉) |
||
熔點 |
|
- |
|
℃(℉) |
|
燃燒性(率) |
|
UL94 |
|
|
|
線性膨脹係數 |
|
ASTM D696/ISO 11359 |
1.28 |
mm/mm.℃ |
|
電氣性能 |
介電常數 |
100HZ |
ASTM D150/IEC 60250 |
|
|
1MHZ |
ASTM D150/IEC 60250 |
|
|
||
介電損耗 |
100HZ |
ASTM D150/IEC 60250 |
|
|
|
1MHZ |
ASTM D150/IEC 60250 |
|
|
||
體積電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω.cm |
|
表面電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω |
|
耐電弧性 |
|
ASTM D495/IEC 60112 |
|
|
|
加工條件 |
乾燥條件 |
|
|
|
|
加工溫度 |
射嘴 |
|
|
℃ |
|
料筒前段 |
|
|
℃ |
||
料筒中段 |
|
|
℃ |
||
料筒後段 |
|
|
℃ |
||
熔體溫度 |
|
|
|
℃ |
|
模具溫度 |
|
|
|
℃ |
|
壓力 |
注塑壓力 |
|
|
Mpa |
|
保壓壓力 |
|
|
Mpa |
||
背壓 |
|
|
Mpa |
||
螺杆轉速 |
|
|
|
rpm |
|
其他 |
備註 |
|
|||
顏色 |
|
||||
特性 |
|
||||
用途 |
|
日本新石油化學 LCP MG350同級別型號
FC-110 G330-NC G345 G-430 HM-302 HM302-BK HM-402 BK MG350-A540 MG-350-B MG350BK
東莞市建和塑膠材料有限公司 | |
---|---|
國家/地區︰ | 广东省东莞市 |
經營性質︰ | 貿易商 |
聯繫電話︰ | 13600184441 |
聯繫人︰ | 黃生 (經理) |
最後上線︰ | 2014/04/04 |