A, composition and characteristic: it is Bi-component face paint with containing hydroxyl acrylic resin as binder, joining various high quality pigment, it has excellent weather resistance, the retenion of color ,tough film and high gloss, not pulverization, no yellowing, good decoration, it also have excellent resistance to chemical properties and water resistance, resistance to mineral oil, vegetable oil, oil solvent and oil products, and resistance to impact and abrasion resistance.

Second, the application: it is suitable for large vehicles, ships, machine table, instrument and other senior product or major projects of steel ,it is also siutable aluminum alloy surface .

Three, performance and technical parameters:

1, color: of all kinds

2, theoretical usage: about 0.15 kg/m2 (in 30 μ m dry film, do not contain the loss)

3, dry film thickness: 30 μ m

4, drying time: face drying time 25 °C ≤2 h

Actual drying time ≤24 h

completely curing 7 d

5, the interval time: 25 °C the shortest 16 h

the longest 2 d

Six, the matching: a (paint) : b (curing agent) = 20:4

7, maturation period: 25 °C 30 min

Four, coating method: brush, roller, high pressure airless spraying, air spray

1, thinner: 103 special thinner

2, Nozzle caliber: nozzle diameter of high-pressure airless spraying: 0.4 - 0.5 mm

Nozzle diameter of airless spraying :2.0 - 2.5 mm.

3.Extrusive pressure: high-pressure airless spraying: 12 to 15 mpa

Airless spraying: 0.3-0.4 MPa.

 

4, Surface treatment: using appropriate method to eliminate the grease, dirt, rust before coating.

Five, storage period : 12 months.

Six, note:

1, first using it after the A and B must stir well according to the proportion of requirements .and using up them in 8 h .

2, when construction tools must ensure that it is dry, clean, and object surface must be clean, no water, no ph. The packaging barrels of rest of the component b must cover tightly in order to not cause the loss.

3, the paint make a, b two component ,so the type of coating must be fully crosslinking and cure completely, after matching with paint it need 0.5h to cure in 25-35 °C temperatures, if the air temperature is below 20 °C ,it should extend aging time.

4, relative humidity shall not be greater than 85% ,otherwise it will be seriously foaming about paint film.

Seven, this relevant data is made from the laboratory, and the actual products may be slightly different.