Principal Feature:

high- carbon and high- chromium alloy tool steel. 

good wear resistance and size ability after heat treatment 

suitable for making long-life high-precision cold-work dies.

Typical Application:

Used for metal stamping die, drawing die, stainless steel sheet blanking die, blanking die with high hardness, shear knife mold, thread rolling die, metal parts production, machinery manufacturing, etc

Heat Treatment:

Forge: at 1020℃-1040℃ Cool slowly and anneal immediately

Annealing: at 650℃-850℃ Cool slowly in furnace

Stress Relieving: at 650℃ Cool slowly to 500℃, then freely in air

Hardening: Preheat at 650℃-750℃ raise to 1020℃-1050℃ Cool in air, oil or into salt bath held at 500℃-550℃ and then air cool