Refractory brick for Aluminum electrolysis Tank

1.Si3N4 Bonded SiC brick for Aluminum refinery

Description

The product is made from high quality Silicon carbide, silica powder, metal Si,by vacuum Nitride Sintering at high temperature.

 

The size&properties of the product can be customized as per your application,&special technical requirement. 

 

Generally,the product has following advantages of:

a.Low thermal conductivity

b.Low thermal expansion

c.Excellent oxidation resistance 

d.Excellent corrosion resistance

e.long duration

Application: 

a.good lining refractory materials in Aluminum electrolysis cell,furnace,kiln,incinerators, and reactors.

b.as Tuyere combined bricks or other combined blocks in Iron&steel industry.

c.Used as Kiln shed board, beams,slide push board, sagger.

Package:Normally,1100kg or1200kg into a Non-fumigated crate,each piece is isolated by good padpaper,bubble film,or foam board,etc..

Note:All of our export package materials confirms to IPPC standard,with an official mark on them.

Parameter:

  

 

item	unit	data
SiC%	≥	72
Si3N4 %	≥	21
Fe2O3 %	≤	0.5
Density	g/cm3	2.65-2.70
Apparent porosity %	≤	18
Modulus of Rupture	Mpa (at ambient temperature)	42
	Mpa(1400℃)	45
Compressive strength	MPA≥	150
thermal conductivity1250℃	W/m.k	15-18
acid-proof alkaline		Excellent
Size Difference	0-100mm	±1.0
	101-300mm	±1.5
	301-500mm	±2.0
	501mm above	±0.5%