Refractory brick for Aluminum electrolysis Tank

1.Si3N4 Bonded SiC brick for Aluminum refinery

Description

The product is made from high quality Silicon carbide, silica powder, metal Si,by vacuum Nitride Sintering at high temperature.

 

The size&properties of the product can be customized as per your application,&special technical requirement. 

 

Generally,the product has following advantages of:

a.Low thermal conductivity

b.Low thermal expansion

c.Excellent oxidation resistance 

d.Excellent corrosion resistance

e.long duration

Application: 

a.good lining refractory materials in Aluminum electrolysis cell,furnace,kiln,incinerators, and reactors.

b.as Tuyere combined bricks or other combined blocks in Iron&steel industry.

c.Used as Kiln shed board, beams,slide push board, sagger.

Package:Normally,1100kg or1200kg into a Non-fumigated crate,each piece is isolated by good padpaper,bubble film,or foam board,etc..

Note:All of our export package materials confirms to IPPC standard,with an official mark on them.

Parameter:

  

 

item	unit	data
SiC%	≥	72
Si3N4 %	≥	21
Fe2O3 %	≤	0.5
Density	g/cm3	2.65-2.70
Apparent porosity %	≤	18
Modulus of Rupture	Mpa (at ambient temperature)	42
	Mpa(1400)	45
Compressive strength	MPA≥	150
thermal conductivity1250	W/m.k	15-18
acid-proof alkaline		Excellent
Size Difference	0-100mm	±1.0
	101-300mm	±1.5
	301-500mm	±2.0
	501mm above	±0.5%

Composite Sidewall Slab for Aluminum Reduction Cell (side wall block,combo brick)

 

Description

With special bonding developed by us,stick graphitic carbon pieces with SiC brick tightly.Can be used directly at Aluminum reduction cells.

The feature:excellent chemical&oxidation resistance,Longer duration,convenient for installation.and so on.

 

Specification:610mm*400mm*75*210mm,or other sizes as per your requirement.

Combo sidewall block for Aluminum electrolysis tank

Description

With special bonding developed by us,stick graphitic carbon pieces with SiC brick tightly.Can be used directly at Aluminum reduction cells.

The feature:excellent chemical&oxidation resistance,Longer duration,convenient for installation.and so on.

 

Specification:610mm*400mm*75/210mm,or other sizes as per your requirement.

Refractory brick for hot blast stove

 

1.Description

Can be used at blast furnace tuyere zone,or refractory lining materials in steel&iron industry.With characteristics of chemical&oxidation resistance,iron slag corrosion resistance,high temperature resistance.

2.Package:Normally,1100kg or1200kg into a Non-fumigated crate,each piece is isolated by good padpaper,bubble film,or foam board,etc..

Note:All of our export package materials confirms to IPPC standard,with an official mark on them.

 

3.Parameter:

item	TDZ-1	TDZ-2
SiC%≥	72	70
Si3N4 %≥	20	20
Fe2O3 %≤	1.5	2.0
Densityg/cm3≥	2.65	2.60
Apparent porosity %≤	17	19
Cold Modulus of Rupture Mpa≥	45	40
Modulus of Rupture (1400) Mpa≥	50	45
Compressive strength MPA≥	160	150
thermal conductivity1000W/m.k	16.0	15.0
acid-proof alkaline		Excellent

 

Refractory brick for copper melting 

1.Description

Made from high quality Silicon carbide, silica powder, metal Si,by vacuum Nitride Sintering at high temperature.

The size&properties of the product can be customized as per your application,&special technical requirement. 

With characteristics of chemical&oxidation resistance,excellent corrosion resistance,high temperature resistance.

2.Package:Normally,1100kg or1200kg into a Non-fumigated crate,each piece is isolated by good padpaper,bubble film,or foam board,etc..

Note:All of our export package materials confirms to IPPC standard,with an official mark on them.

 

3.Parameter:

item	Furnace lining brick	Shapes brick
SiC%≥	70	70
Si3N4 %≥	20	20
Densityg/cm3≥	2.65	2.60
Apparent porosity %≤	17	18
Cold Modulus of Rupture Mpa≥	45	40
Modulus of Rupture (1400) Mpa≥	50	45
acid-proof alkaline		Excellent