High Alumina Ceramic Setter Plate  High Temperature Kiln Furniture 

1.Bending Resistant Setter Plates： 
 AL2O3：89.5%    Operating Temperature：1650℃ 
 Thermal Expansivity：≈5.5    Flexural Strength(at 1400℃)：13.5mpa;
2.Bearing Setter Plates： 
 AL2O3：90.5%    Operating Temperature：1650℃ 
 Thermal Expansivity：6.5-7.0   Flexural Strength(at 1400℃)：14.5mpa;
3.Color：White
4.Common Size：300×300mm, 320×200mm, 230×200mm, 250×230mm, 230×125mm, 250×180mm,  200×200mm etc.

Production Feature
* High corrosion-resistance.
* High mechanical strength.
* Lower possibility of crack by thermal shock.
* Longer service time.

Different Types of Alumina
Aluminas are generally white but are sometimes pink (88% alumina) or brown (96% Alumina). The colour is derived from either the sintering additives or impurities in the raw materials. Dynamic-Ceramic produces a range of alumina from 96% - 99.9% purity.

Properties of Alumina
Alumina has a high melting point, high hardness and high mechanical strength, although mechanical strength is reduced at temperatures above 1000°C. Due to the relatively large coefficient of thermal expansion, thermal shock resistance is reduced. Alumina is an electrically insulating material, with a high electrical resistivity, increasing with purity.Good chemical stability of alumina, leads to a high corrosion resistance. It is insoluble in water and only slightly soluble in strong acid and alkaline solution.

Various Application
* Seal rings
* Medical prostheses
* Laser tubes
* Electronic substrates
* Ballistic armour
* Thermocouple tubes
* Electrical insulators
* Grinding media
* Threadguides
* Wear components

About UniPreTec
UniPreTec provides high-performance ceramic products in Alumina, Zirconia, Zirconia Toughened Alumina, Silicon Carbide, Silicon Nitride and  further special materials. Along with these materials, we offer several machining from which to choose such as cutting, drilling, sawing, turning, grinding, polishing etc.. Furthermore, our technologies and equipments allow us to provide various and flexible forming processes, like dry pressing, isostatic pressing, extrusion, injection moulding and slip casting.