Surface treatment : hot dip galvanized

Zinc thickness: 86μm

Technology: press ,cut ,drop forged

Load : 70kn/120kn/160kn

Voltage : 11kv/33kv

Life time: more than 30years

Used on : overhead line

Color: Silver

advantage: good price with high quality

Experience: More than 12years.

Used with: ball eye ,ball socket , tension clamp, U bolt

Export to : Allover the world

Certificate : ISO9001, SGS

Product description:

electric power fitting Dimensions:

The dimensions on the drawings are the final dimensions after the hot dip galvanization. The design of the fittings is indicative; however the mentioned dimensions on the drawings are the critical ones.

electric power fitting GALVANIZATION

The fittings shall be delivered hot dip galvanized according to the following specifications:

• The Zinc of the electric power fitting  that shall be used shall have the quality of minimum category prime western according to  the category Zn 98.5 according to ISO-1461.
• Then washed out with water and then flux treated and dried out.
• The hot dip galvanization shall be made in a Zinc bath of temperature 450°C and of Zn-composition min. 98,5%.
• The galvanization thickness of the electric power fitting shall be in average 80m thick! On an isolated piece or on a small part of the surface the thickness can be a little lower, however on all pieces and on all surfaces the minimum thickness shall be 78μmand the average weight in relation to the galvanized area shall be 610 gr/m2.
• The pieces of the electric power fitting shall be after HDG free from black stains, enclosures of dirt, knobs, bubbles or any other surface defects. The HDG shall be smooth and uniform in the entire piece without any spots with too small or too big galvanization thickness otherwise the pieces will be rejected.
• The galvanization shall stick very well on the steel structure; it shall not be removed as a film but shall be as one with the steel body