Packing specification of BD708 wear resistant impact resistant coatings: 
Two component,20Kg/group,packed in a drum  

performance feature of BD708 anti wear impact resistant coating:
   1.  Two component,black daub shape,can cure at room temperature,heat for curing can get better comprehensive properties.
   2.  Excellent in wear & corrosion & impact resistance,the wear resistance is 5 times more than PU rubber,20 to 30 times more than common mixing rubber,the impact. resistance is 10 to 15 times more than imported wear resistant protective agent.
   3.  Can single use,with the better bonding strength to metal substrate through using it together with primer.
   4.  Can be blade coating,easily forming,construction is convenient,can achieve seamless coverage of equipment overflowing parts.
   5.  Suitable for the partial repairing and whole protecting of the quipment under the working condition of higher wear & impact resistant requirements.

product usage of BD708 anti abrasion impact resistant coatings:
　   BD708 impact & wear resistant coatings is the high performance wear & impact resistant polymerization material compounded by high performance wear resistant aggregate(silicon carbide,alumina,carborundum etc.) and special high polymer material.It can be blade coating,with good water resistance and high bonding strength,excellent in wear & impact resistance. Used in the wear repairing of equipment overflowing parts and the preparation of impact & wear resistant coatings on the whole equipment overflowing parts,exclusively used in the surface wear repairing of magnetic separator roller or the preparation of wear & impact resistant coatings on the roller surface directly,exclusively used in repairing chute,centrifuge and ball mill end cover

How to use of BD708 impact resistant abrasion resistant coating:
  1.  Surface treatment: Do coarsening treatment on the pending-repair part,(sand blasting treatment will get the best effect,if it doesn't have sand blasting condition,can do grinding treatment with angle grinder),the surface after coarsening treatment should be cleaned by cleaning agent(can use acetone,ethyl acetate etc.),then dry it by airing,the surface after this treatment should be the coarsening,clean and fresh metal substrates.
   (Make the special undercoat of  BD708 impact & wear resistant coating mix uniformly according to specified percentage,and brush coating on the substrate surface,then wait for the undercoat curing)
  2.  Preparation:After undercoat fully curing,according to the specified ratio,make A and B component of BD708 impact & wear resistant coating mix uniformly,and use it up within 30 min.Generally it’s while construction and configuration.Every time the most configuration quantity is not more than 5Kg,every time configure too much adhesives,the curing speed is fast,hasn't been used up until the adhesive has already partial cured and can't be used.
  3.  Coating:The suitable coating thickness of  BD708 impact & wear resistant coatings  is 3~10mm,make the mixed-up material be coating on the undercoat surface,the adhesive layer should be compacted.Repair the surface to be smooth after the coating is coated on the required size.
  4.  Curing condition:s est curing for 72 hours before putting into use,if needing instant-on,can heat it up to 80℃ slowly and keep this temperature for about 3 hours after room temperature curing for 4 hours.

performance index:

Transportation storage of wear & impact resistant coatings:
       Sealed storage in the cool and dry place.The warranty period is 4 months.Avoid placing it upside down,knocking against and transporting it as a non-dangerous product during transportation.