Product instruction
BiogoTM double-component waterproofing coating belongs to solidify waterproof materials, and the Group A is isocyanate terminated pre-polymer polycondensated by polyether and isocyanate, Group B is colored liquid composed of plasticizer, curing agent, thickening agents, coagulant agent and filler, ,ix Group A and B evenly as rate and brush on the waterproofing substrate surface, form a elastics and rubber-like coating film through cross-linking and solididying at normal temperature, which plays a role of waterproofing
Characteristic
BiogoTM double-component waterproofing coating forms seamless, integrate elasticity waterproof layer solidifying, and improve waterproof and seeping resistance of the project, which is waterproof membrane that can not be attained. Especially the coating film has high elasticity and elongation, high adaptability to substrate craking or expansion.
Firm bonding with substrate, coating film has extreme bonding power with concrete, timber, metal, pottery and asbestos shingle, also can be used as bond.
Convenient application, polyurethane coating film is a cold application waterproof coating, just mix group A and B as rate when application and brush it on the waterproof substrate.
Easy maintenance, only maintain the broken parts, which can reach the original effects of waterproofing, save time, save power and low cost.
Environmental product, and reduce the damage to the person and environment.
Technical property [Execute standard GB/T19250-2003]
No. |
Item |
Index |
||
I |
II |
|||
1 |
Solid content%≥ |
92 |
||
2 |
Dry time of outside/inside h≤ |
Drying time of outside |
8 |
|
Drying time of inside |
24 |
|||
3 |
Tensile strength MPa≥ |
1.9 |
2.45 |
|
4 |
Fracture elongation%≥ |
450 |
450 |
|
5 |
Water impermeability 0.3MPa, 30min |
Impermeable |
||
6 |
Bending at low temperature ≤ |
-35 |
||
7 |
Bonding strength of moist base a MPa≥ |
0.5 |
||
a. only use the moist substrate of underground project. |
Application technology
Ingredient and dosage: according to application dosage, evenly mixing round o us.
Large waterproof application, coating uniformity mixed coating with a rubber or plastic scraper, the thickness is onsistent, generally it is 1.5mm to 2.0mm, should be brushed in 3 to 4 times, the last time brushing should be done after the pervious brushing cures and becomes film, and brushing at a ertical direction. Generally as a separate film-forming, for underground project board, should pave a layer of felt reinforced material in addition
Coating thickness: To underground project thickness is 1.2 to 2.0mm, generally 1.5mm; to toilet thickness is not less than 1.5mm; to multilayer waterproof of exposured roof construction thickness is not less than 1.2,,; to one layer waterproof of grade Ⅲ waterproof, thickness is not less than 2mm;
Finishing layer application: scatter the cleaned sand before the last time brushing is not solidified.
Protection layer: on the coating film surface should do insulation protection as the design.
Attention
Storage and attention items
Applicable scope
Widely used in roofs, basement, swimming pool, and all kinds of industry and civil building waterproofing.
weifang hongyuan waterproof materials co.,ltd | |
---|---|
Country/Region: | Shan Dong - China |
Business Nature: | Manufacturer |
Phone: | 15163601048 |
Contact: | ellen (sales) |
Last Online: | 24 May, 2016 |