1.2714 Tool Steel

Standards	DIN	AISI	JIS	ГОСТ
X55NiCrMoV7	1.2714	L6	SKT4	5ХН2МФ

ALTA SPECIAL STEEL supply DIN 1.2714 / AISI L6 in round bar, plate, square, sheet and block.

Nickel-chrome-molybdenum-vanadium steel for hardening in the stream of air or in oil with high hardenability. The steel has high hardness after hardening, good resistance to the tempering, good toughness and good firmness during the heat. Is resists quick temperature changes and also thermal fatigue. The steel is well-workable during the heat and well-workable in the soft-annealed state.

We welcome your inquiries for tool steel, please contact us for quotation sales@altaspecialsteel.com

_________________________________________________________________________________________

Chemical Composition

C	Si	Mn	P	S	Cr	Mo	V	Ni
0.50-0.60	0.10-0.40	0.65-0.95	≤0.030	≤0.030	1.00-1.20	0.45-0.55	0.07-0.12	1.50-1.80

Product Range

Round bars : Dia 16mm - 800mm

Flat bars : Thick 50mm - 405mm, width up to 1000mm

_________________________________________________________________________________________

Applications : for tools for mechanical working during the heat such as dies of all sizes, especially with the firmness over Nmm2 for drop hammers and forging presses, extruders with the firmness over 1600 Nmm2 for extrusion of non-ferrous metals. The steel is appropriate for knives during the cold cutting of materials of thick thicknesses, knives for scrap iron. For pressing of plastic substances, big forces and breeze-blocks can be produced from this steel and these can be hardened in air.

_________________________________________________________________________________________

Heat Treatment

Way	Temperature[℃]	Remark
Forging	850 - 1050
Soft annealing	680 - 710	Max. 248HB after annealing
Quenching	840 - 860	Cool in oil up to about 100 °C
Tempering	490 - 510