Charging pile cable material granulation machine production line

The new energy charging pile low smoke halogen free cable material is the twin screw high speed, strong mixing and single screw low speed, low temperature, weak shear characteristics, the process of high degree of automation, pipeline operations, the dispersion effect is excellent, high yield, condition of clean, is the heat sensitive material, high shear mixing modified models. Low smoke halogen-free cable material granulator unique with slide of blowing die surface eager to head, the head part is cooled, single screw core cooling, effectively prevent the clay in the production process, yield increased significantly.

Precautions

1, broken and materials may be used after drying, the remaining material immediately sealed to prevent moisture. Drying condition: drying oven at 70 ℃8 hours (material thickness 2-4cm), or vacuum-dried for more than 4 hours.

2, before use to ensure that the screw, barrel, feeding bucket completely clean, processing is prohibited to bring water and impurities.

3, the user can customize according to the needs of various masterbatch added s ested masterbatch added in a proportion of 0.2% to 0.8%; in order to achieve the best extrusion results, we recommend masterbatch added in the 70 ℃oven drying 8 hours or more (the thickness of material 1-2 cm), or more than 4 hours and dried in vacuo.

4, 4, if the storage time of more than 2 months to use, it is best to pre drying, drying conditions: 70 degrees in the oven drying 8 hours or more (material layer thickness 2-4cm), or vacuum drying for more than 4 hours.

Packaging Storage

1, the plastic composite bag with plastic composite bag packaging, each bag is 25kg.

2, should not be exposed to the sun and rain in the transport process, in the process of handling should be handled with care, to avoid mechanical damage and other abnormal conditions of infringement, should be placed in a cool, ventilated and dry warehouse.