kovar material Iron-Nickel-Cobalt Alloys glass to metal Applications

kovar material Iron-Nickel-Cobalt Alloys glass to metal Applications
Model:4J29
Brand:xagy
Origin:Made In China
Category:Metallurgy , Mining & Energy / Metallurgy & Mining / Bars, Rods, Angles, and Stainless Steel Shapes
Label:kovar , kovar material , glass to metal
Price: US $21 / pc
Min. Order:10 pc

Product Description

Kovar Alloy® standard specification for Iron-Nickel-Cobalt Sealing Alloy 

Sheet             Thickness:0.1mm~3.5mm

Plate              Thickness:3.5mm~4.0mm
Bar                 Dia 32.0mm~Dia180.0mm

Pipe               OD 120mm~8.0mm,ID 8.0~129

Wire               Dia 0.1mm-Dia5.0mm

 

Products Application                                                                    

It is applied to hard glass to metal seals 

ddf1d48d-811d-4699-b396-b100e591889a (1).jpg

Description                                                                                  

 Kovar Alloy  is a vacuum melted, iron-nickel-cobalt, low expansion alloy whose chemical composition is controlled within narrow limits to assure precise uniform thermal expansion properties. Extensive quality controls are employed in the manufacture of this alloy to ensure uniform physical and mechanical properties for ease in deep drawing, coining, stamping and machining.  

 

Parameter                                                                                   

     TABLE 1      Chemical Requirement                                                                                                           

Element                                                                                 Composition,%                                                                  

C  ≤                                                                                                                                   0.03

P≤                                                                                                                                      0.020

S≤                                                                                                                                      0.020

MN≤                                                                                                                                   0.50

SI≤                                                                                                                                     0.30

CU≤                                                                                                                                   0.20

CR≤                                                                                                                                   0.20

MO≤                                                                                                                                   0.20

NI                                                                                                                                    28.5-29.5    

CO                                                                                                                                 16.8-17.8

FE                                                                                                                                   remainder                                                                       

Notes:

1.Under the condition that the average coefficient of the linar expansion meets the requirements of the standard,the content of nickel and cobalt are allowed to deviate from the stated range.

2.the shape and dimensions of the alloys are in compliance with GB/T14985

 

       TABLE 2                                       Physical Requirement                                                                    

Property                                                                                                        Target                                                              

Specific gravity                                                                     8.36

Density                                                                                 lb/cu in 0.302             /        kg/cu m 8359

Thermal conductivity                                                            Btu-in/ft²/hr/°F120       /       W/m-K173

Curie temperature                                                                °F815                          /       435°C

Melting Point                                                                         °F 2640                       /       °C1450

Modulus of elasticity                                                             psi x 10(6) 20               /       psi x 10(6) 138

Electrical resistivity                                                               ohm-cir mil/ft 294          /      microhm-mm 490                                 

 

     TABLE 3                                   Tensile Strength  of wire                                                                        

Symbol                                  Status                                     Tensile Strength/MPa                                                         

R                                             annealed                                                <585

1/4 I                                         1/4hard                                                 585-725

1/2I                                          1/2hard                                                 655-795

3/4I                                          3/4hard                                                 725-860

   I                                            unannealed                                             >860                                                                        

 

     TABLE 4                                   Tensile Strength  of strip                                                                         

Symbol                                         Status                                        Tensile Strength/MPa                                               

R                                                 annealed                                                <570

1/4 I                                             1/4hard                                                 520-630

1/2I                                              1/2hard                                                 590-770

3/4I                                              3/4hard                                                 600-770

   I                                               unannealed                                              >700                                                                  

 

     TABLE 5                             Hardness of Deep Stamping Strip                                                             

State                                           Thickness                                        Hardness,HV                                                       

                                                       >2.5                                                    170

Deep Stamping                               ≤2.5                                                    165                                                                 

 

    TABLE 6                             Coefficient of Linear Expansion                                                                    

          Heat Treatment of the Sample                                          20-300°C           20-400 °C           20-450 °C                    

Heat to temperature of 900±20℃ in the hydrogen,

hold for 1h;re-heat to 1100±20℃, hold for 15 min.;

cooled to 200℃ at a rate less than 5℃/min                                                                 4.6-5.2                  5.1-5.5                        

 

   TABLE 7             Coefficient of Linear Expansion                     

Sample 1.    L 24.45mm      Sample 2.   L 25.09mm       (ø6-ø10mm bar ±0.1)                                

4J29 16060701-SiO2416-803 416-804 S1.png

Product Detail                                                                             

conew_img_0518.jpg

2012_6_4_9_56_40_4625_conew1.jpg

IMG_0682.jpg

Why Us ?                                                                                                                           

photobank (3)_0011.jpg

IMG_9420_conew2.jpg

1.Specialized in manufacturing high-precision alloy for 23+ years

2.We can tailoring your unique requirements with ASTM, UNS ,GOST, standards.

3. We can produce more people cannot produce products

4. Short Lead-time

5. Leading Edge Technology

6. Good quality control in production process, ISO9001:2008, SGS, CQC, approved.

7. Excellent quality and High cost of performance

8. Available in an extensive range of stock or custom size.

9. The whole process from raw material to finished products can be traced.

10. 40000 square meters workshop, advanced facilities and test equipment .                                                        

 

Our Serivce                                                                                                                                                                   

1. Free Sampe with test report 

2.Small Quantity  accepted , if we have stocks, we can delivery as small as few kilogram to your specification. 

3.Testing services available .

4.Inspection before delivery 

5.Response within 24hours 

6.Good after service 

 

kovar material Iron-Nickel-Cobalt Alloys glass to metal Applications 1kovar material Iron-Nickel-Cobalt Alloys glass to metal Applications 2kovar material Iron-Nickel-Cobalt Alloys glass to metal Applications 3kovar material Iron-Nickel-Cobalt Alloys glass to metal Applications 4kovar material Iron-Nickel-Cobalt Alloys glass to metal Applications 5

Member Information

xi'an gangyan special alloy co.ltd
Country/Region:Shaan Xi - China
Business Nature:Manufacturer
Phone:13669288752
Contact:paul (sale manger)
Last Online:14 May, 2019