Ni-Span C 902®Standard Specification for Nickel-iron-Chromiumobalt Alloys 

Sheet             Thickness:0.1mm~3.5mm

Plate              Thickness:3.5mm~40.0mm
Bar                 Dia 5.0mm~Dia180.0mm

Pipe               OD 120mm~8.0mm,ID 8.0~129mm

Wire               Dia 0.1mm-Dia5.0mm

 

Products Application                                                                    

They are usually used for making instruments, wireless elastic sense organs, bellows, diaphragms.

Description                                                                                  

A precipitation hardenable Nickel-Iron-Chromium alloy having outstanding controllable thermoelastic coefficient characteristics and excellent oxidation resistance in high temperature atmospheres. The alloy can be processed to have a constant modulus of elasticity at temperatures ranging from -45 to +65oC (-50 to +150oF).

 

Parameter                                                                                   

    TABLE 1           Cross Reference                                                                                                                        

Contury                                         Name 1                                       Name 2                                                                            

Russia                                          42HXTΙΟ                                     H42XT                                                    

USA                                              Ni-Span c902                              Elinvar

Germany                                      Ni-Span C

UK                                                Ni-Span C

Japan                                           Sumispan-3                                 EL-3                                                                              

 

     TABLE 2      Chemical Requirement                                                                                          

Element                                                                                 Composition,%                                                                   

C  ≤                                                                                                0.05

Si≤                                                                                                 0.80

P≤                                                                                                  0.020

S≤                                                                                                  0.020

Mn≤                                                                                                0.80

Ni≤                                                                                                41.5-43.0

Cr                                                                                                 5.20-5.80

TI                                                                                                  2.3-2.70

Al                                                                                                  0.5-0.8

FE                                                                                                remainder                                                                         

Notes:

1.the shape and dimensions of the alloys are in compliance with YB/T5256-1993

 

       TABLE 3            Physical Requirement                                                                                                        

Property                                                                                                    Target                                                                    

Density                                                                                                        8.0                

Modulus of Elasticity(E/Empa)                                                             176500-191000

Shear eleasticity(G/MPa)                                                                      63500-73500

Vickers Hardness(HV)                                                                                350-450

Staturation induction density(B600/T)                                                           0.7

Mean Coefficient of Linear Expansion20-100℃(10-6/K)                                 8.5

Resistivity p/(Ω°m)                                                                                           1.1                                                                

 

     TABLE 4            Yield Strengh(after the heat treatment)                                                                         

Delivery State                                  Thickness/mm                   Yield Stength/Mpa                                                                    

Annealed                                          0.50-2.50                               <685

Cold rolled                                          0.50-1.00                                 >885                                                                              

 

     TABLE 5            The temperature coefficient of the modulus of elasticity                                 

 Aging Temperature/℃            The temperature coefficient of the modulus of elasticityβE/(10-6/℃)(-6~+80℃)

                                                                          Cold Rolling                                  Annealed                                               

500                                                                      -38~15                                        +18~+12

550                                                                      -22~0                                          +10~+35

600                                                                       0~+20                                         +35~+55

650                                                                       0~+20                                         +42~+64

700                                                                       0~+20                                         +40~+60                              

750                                                                       -4~+16                                        +28~+50                                               

 

    TABLE 6            Mechanical property requirement                                                                                                     

Shape        Delivery State       Thickness&Diameter/mm        Tensile Strengthòb/MPa           Elongationò(%)≥                               

Strip            Annealed                0.20-0.50                                    <885                                      20
Wire            Cold Drawn             0.20-3.0                                       >930                                                                               

 

Product Detail                                                                             

Why Us ?                                                                                    

1.Specialized in manufacturing high-precision alloy for 23+ years

2.We can tailoring your unique requirements with ASTM, UNS ,GOST, standards.

3. We can produce more people cannot produce products

4. Short Lead-time

5. Leading Edge Technology

6. Good quality control in production process, ISO9001:2008, SGS, CQC, approved.

7. Excellent quality and High cost of performance

8. Available in an extensive range of stock or custom size.

9. The whole process from raw material to finished products can be traced.

10. 40000 square meters workshop, advanced facilities and test equipment .                                                        

 

 

Our Serivce                                                                                                                                                      

 

1. Free Sampe with test report 

2.Small Quantity  accepted , if we have stocks, we can delivery as small as few kilogram to your specification. 

3.Testing services available .

4.Inspection before delivery 

5.Response within 24hours 

6.Good after service