Model: | POK M630A |
---|---|
Brand: | HYOSUNG |
Origin: | Made In Korea |
Category: | Chemicals / Resin |
Label: | Korea HYOSUNG , POLYETONE , POK/M630A |
Price: |
¥24.5
/ kg
|
Min. Order: | 25 kg |
Density | 1.24g/cm³ | Melt flow index 240°C/2.16kg | 6g/10min |
Melting temperature | 222℃ | Water absorption at Saturation | 2.1% |
Tensile elongation at break | 200% | Notched Charpy impact strength | 15KJ/㎡ |
Tensile strength at yield | 57MPa | Tensile modulus | 1450MPa |
Flexural strength | 53MPa | Flexural modulus | 1350MPa |
Special performance:
1. High impact strength: Compared to Nylon, PBT has a 230% higher impact strength.
2. Hydrolysis resistance: No formaldehyde precipitation, certified for water treatment safety by KTW and W270, non absorbent and non deformable. Maintain high tensile and impact strength under wet conditions, and have a high elongation.
3. Chemical resistance: Acid and alkali resistant, second only to PPS in chemical resistance.
4. Fuel resistance: After professional testing, POK has stronger fuel resistance than PA11 and PA12.
5. High barrier properties: Belongs to hydrocarbons. Through the permeability test of lead-free gasoline at @ 93 ℃ * 15 days, it is superior to PTFE and has a gas barrier comparable to EVOH.
6. Superior friction performance: The wear resistance of ordinary models is three times that of POM, with excellent low noise. The wear resistance of wear-resistant models is more than ten times that of POM, with almost no noise.
7. High energy production efficiency: High crystallinity polyketones help shorten the molding cycle. The production cycle is approximately two-fifths of PA66.
8. Green and environmentally friendly: synthesized from carbon monoxide, which is one of the main sources of atmospheric pollution; Free from harmful substances such as formaldehyde.
Shenzhen Juhong New Material Co., Ltd. | |
---|---|
Country/Region: | Guang Dong - China |
Business Nature: | Trading Company |
Phone: | 17317553198 |
Contact: | XIANLONG PAN (Service Manager) |
Last Online: | 04 Sep, 2024 |