DC-C30 RTV-2 Mold Making Silicone Rubber is used for making molds of concrete stone, GRC(Glass-fiber Reinforced Composite), gypsum decoration, plaster ornaments, polyester decoration,, polyresin crafts, polyurethane, bronze, wax, candle, and similar products

DC-C30 RTV-2 Mold Making Silicone Rubber is  room temperature vulcanized silicone rubber in condensation type. It’s named as two part silicone rubber, Part A is a flowable liquid silicone, Part B is the curing agent (Tin catalyst) . It’s mainly used for mold making.

Technical Parameters

DC-C30 Silicone rubber with moderate hardness in high tensile and tear strength,which is suitable for middle or large size product with pattern by both pouring and brushing operation,especially popular for manufacturer of gypsum decoration and concrete molding,It is one of our best selling silicone. 

Model	Color	Mixing ratio (%)	Pot life (mins, under 25℃)	Curing time (hrs,under 25℃ )	Hardness ( Shore A )	Tensile- strength  (MPa)	Tear- strength (kN/m)	Viscosity （After A/B mixed ,mPa.s）	Shrinkage rate (%)	Elongation （%）
DC-C30	White	2	30-40	3-5	30±2	>4.2	>25	27000±5000	≤0.25%	>450%

Characteristics 

1.High tensile and tear strength

2.Good flexibility

3.High duplication times

 

Operation instructions

Step 1: prepare the original molds

Make your original molds perfect. fix it on a board. And fix the original mold on a board , then used four piece of board to enclose the original molds .

Step 2: Take 100 G parts A and add 2G parts B and mix them evenly.

Notes: Mold making silicon rubber is a kind of flowing liquid ,it contains two parts. Part A is a kind of flowing white liquid and part B is the curing agent or catalyst .Pls follow the step strictly:

         1.Weigh the two part exactly by electronic weight. If not, for example add too much catalyst , the operation time will be too fast to operate ,which will cause inconvenience to operate . 

 

2.Mix part A and part B evenly. Otherwise the silicon rubber will be partly solidified and this will give birth to difficulties in your final operation. What’s more, the finished molds will meet a short life. All of these will cause a waste of silicon rubber.

 

Step 3: Vacuum pumping

Without exception, this step takes less than 10 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available.

 

Step 4: Pouring casting or Brush operation

Notes:1. For simple pattern products we s est use pouring operation way, which will be very easy to operate and demould. Pourable silicone require low viscosity which will be easy to flow smoothly and easy to de-air .

        2.For delicate pattern products we s est use brushing operation way, which can copy the pattern exactly . Brushable silicone require high viscosity which won’t be easy to flow away and easy to brush .  

        3. We s es to set the silicone mold for another 12 hours after demould before you put it into a large production .

Shelf life

Twelve(12) months when stored under dry and cool place by original package under 25℃

Package
25KG/drum vacuum packing for part A +1kg/ bottle catalyst for part B;9/18drums/pallet;

200KG/drum packing for part A +1kg/ bottle catalyst for part B; 1//2/4drums/pallet;

Minimum order of quantity(MOQ)

200KG