Heating Elements

MoSi₂ is a conductive silicide that is oxidation-resistant because of the formation of stable silica layers on its surfaces at high temperatures.

MoSi₂ has been produced as an electric heating element for use in air, at temperatures beyond 1600 °C. A known commercial MoSi₂ heating element is cermet, which is made by bonding a mixture of MoSi₂ particles together with an aluminosilicate glass phase, usually as 20% of the total volume.

 

Although top-grade MoSi₂ elements can function at temperatures of up to 1800 °C, the material is highly brittle and can suffer severely from creep during use. However, they offer process benefits as they can work at high electrical loads without aging, and do not exhibit increasing electrical resistivity during use. They are oxidation-resistant in air, oxygen, and oxygen-rich atmospheres.

Moreover, they can be used with ammonia, nitrogen, hydrogen, noble gases, and limited vacuum, but operating temperatures and service life may be decreased because of the failure of the protective oxide layer.

 

MoSi₂ elements come as readymade elements and are manufactured as either bent or straight forms, in an extensive range of dimensions. The elements are primarily used in production furnaces and laboratory furnaces in the ceramics, glass, steel, electronics, and heat-treatment sectors.

 

 

Atmosphere	Max. element temperature
	MS1700	MS1800
Air	1700℃	1800℃
Nitrogen	1600℃	1700℃
Argon, Helium	1600℃	1700℃
Hydrogen	1100-1450℃	1100-1450℃
N2/H2 95/5%	1250-1600℃	1250-1600℃

 

Chemical Properties of Physical Properties of Mosi2 Heating Rod

 

Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.

Heating Elements

MoSi₂ is a conductive silicide that is oxidation-resistant because of the formation of stable silica layers on its surfaces at high temperatures.

MoSi₂ has been produced as an electric heating element for use in air, at temperatures beyond 1600 °C. A known commercial MoSi₂ heating element is cermet, which is made by bonding a mixture of MoSi₂ particles together with an aluminosilicate glass phase, usually as 20% of the total volume.

 

Although top-grade MoSi₂ elements can function at temperatures of up to 1800 °C, the material is highly brittle and can suffer severely from creep during use. However, they offer process benefits as they can work at high electrical loads without aging, and do not exhibit increasing electrical resistivity during use. They are oxidation-resistant in air, oxygen, and oxygen-rich atmospheres.

Moreover, they can be used with ammonia, nitrogen, hydrogen, noble gases, and limited vacuum, but operating temperatures and service life may be decreased because of the failure of the protective oxide layer.

 

MoSi₂ elements come as readymade elements and are manufactured as either bent or straight forms, in an extensive range of dimensions. The elements are primarily used in production furnaces and laboratory furnaces in the ceramics, glass, steel, electronics, and heat-treatment sectors.

 

 

Atmosphere	Max. element temperature
	MS1700	MS1800
Air	1700℃	1800℃
Nitrogen	1600℃	1700℃
Argon, Helium	1600℃	1700℃
Hydrogen	1100-1450℃	1100-1450℃
N2/H2 95/5%	1250-1600℃	1250-1600℃

 

Chemical Properties of Physical Properties of Mosi2 Heating Rod

 

Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of element owing to the high temperature combustion, which prevent Mosi2 from oxidizing more. When the element temperature is higher than 1700 °C, the film becomes melting. It’s not suitable for long time use in the temperature range of 400-700°C, otherwise, the element will be powdering for the strong oxidation under low temperature.